Preformed sheet and ballistic-resistant article
The invention relates to a preformed sheet comprising mono-layers from a fibrous network with fibers having a tensile strength of at least about 1.2 GPa and preferably a binder, and a separating film on at least one of its outer surfaces, the separating film having an areal density of between 1 and 10 g/m 2 and a surface tension of less than 35 mN/m at the surface faced to the fibrous network and the separating film has a crystallinity of between 50 and 90%.
1. A preformed sheet comprising at least two mono-layers, wherein each mono-layer comprises:
a fibrous network comprised of fibers having a tensile strength of at least 1.2 GPa and a binder, and
a separating film on at least one outer surface of the mono-layers, wherein
the separating film is substantially free of voids or porosity and exhibits (i) an areal density of between 1 and 10 g/m 2 , (ii) a surface tension of less than 35 mN/m at a surface of the separating film facing the fibrous network and (iii) a crystallinity of between 50 and 90%.
2. The preformed sheet according to claim 1 , wherein the mono-layer comprises a layer of unidirectionally oriented fibers.
3. The preformed sheet according to claim 2 , wherein a fiber direction of one mono-layer is rotated relative to a fiber direction of an adjacent mono-layer.
4. The preformed sheet according to claim 1 , wherein the fibers comprise ultra-high molar mass polyethylene.
5. The preformed sheet according claim 1 , wherein the binder is a thermoplastic polyolefin.
6. The preformed sheet according claim 1 , wherein the binder is styrene ethylene butylene styrene copolymer (SEBS) or styrene isoprene styrene (SIS).
7. The preformed sheet according to claim 1 , wherein the separating film is a biaxially stretched polyolefin film.
8. The preformed sheet according to claim 7 , wherein the separating film is a biaxially stretched polypropylene (BOPP) film.
9. An assembly which comprises at least two of the preformed sheets according to claim 1 .
10. A ballistic-resistant article comprising at least one assembly according to claim 9 .
11. The ballistic-resistant article according to claim 10 , wherein the assembly has an areal density less than 4.75 kg/m 2 and V50 of at least 600 m/s against 9 mm, wherein the article has a 9 mm V50 retention after 24 hours soaking in salt water, and after 4 hours in JP8 fuel of at least 85%.
12. A ballistic-resistant article comprising at least one preformed sheet according to claim 1 .
13. The ballistic-resistant article according to claim 12 , wherein the at least one preformed sheet has an areal density less than 4.75 kg/m 2 and V50 of at least 600 m/s against 9 mm, wherein the article has a 9 mm V50 retention after 24 hours soaking in salt water, and after 4 hours in JP8 fuel of at least 85%.