Mg-containing Zn alloy coated steel
View Patent ↗A Mg-containing Zn alloy coated steel including a steel and a metallic coating layer placed on a surface of the steel, in which the metallic coating layer is a layered structure of plural flat-form metal particles having a particle diameter of from 5 to 100 μm, and a thickness of from 0.5 to 30 μm, the composition of the metal particles include Zn from 11 to 80 mass %, Al from 3 to 80 mass %, Mg from 8 to 45 mass %, and Ca from 1 to 5 mass %, and the Zn, Al, and Mg content satisfy Zn+Al>Mg, and in which the metal particles include a quasicrystalline phase, an MgZn 2 phase, and optionally a balance structure.
1. An Mg-containing Zn alloy coated steel, comprising:
a steel; and
a metallic coating layer placed on a surface of the steel, wherein:
the metallic coating layer is a layered structure of plural flat-form metal particles having a particle diameter of from 5 to 100 μm, and a thickness of from 0.5 to 30 μm,
a composition of the metallic coating layer satisfies, in terms of % by mass: Zn being from 11 to 80%, Al being from 3 to 80%, Mg being from 8 to 45%, Ca being from 1 to 5%, and Zn+Al>Mg, and
the structure of the metallic coating layer comprises a quasicrystalline phase, an MgZn 2 phase, and optionally a balance structure, wherein a total area fraction of the quasicrystalline phase and the MgZn 2 phase is 45% or more, an area fraction of the balance structure is from 0 to 55%, an area fraction of the quasicrystalline phase is 20% or more, and an area fraction of the MgZn 2 phase is 3% or more,
wherein an area fraction of the structure of the metallic coating layer is determined from a cross-section cut in a thickness direction of a coating layer.
2. The Mg-containing Zn alloy coated steel according to claim 1 , wherein a Al content is from 3% to less than 13% in terms of % by mass.
3. The Mg-containing Zn alloy coated steel according to claim 1 , further comprising an oxide film covering a surface of each metal particle, wherein the oxide film has a film thickness of from 1 nm to 1000 nm.
4. The Mg-containing Zn alloy coated steel according to claim 1 , wherein the metallic coating layer is a thermal spray coating layer.
5. The Mg-containing Zn alloy coated steel according to claim 1 , wherein the composition of the metallic coating layer further comprises one or more of Y, La, Ce, Si, Ti, Cr, Co, Ni, V, Nb, Cu, Sn, Mn, Sr, Sb, Pb, C, Fe, and Cd; and
wherein the following Formula (A), and the following Formula (B) are satisfied:
Ca+Y+La+Ce≤3.5% Formula (A)
Ti+Cr+Co+Ni+V+Nb+Cu+Sn+Mn+Sr+Sb+Pb+C+Fe+Cd≤0.5%; and Formula (B)
wherein, in Formula (A) and Formula (B), an element symbol stands for the content of the element in terms of % by mass; and
wherein, if the composition further comprises Si, Si is present at up to 3.5% by mass.