Denitration catalyst and method for producing the same
There is provided a catalyst that exhibits a high denitration efficiency at a relatively low temperature and does not cause oxidation of SO 2 in a selective catalytic reduction reaction that uses ammonia as a reducing agent. A denitration catalyst is obtained by coating a substrate with a catalyst component. The catalyst component contains 43 wt % or more of vanadium pentoxide and has a BET specific surface area of 30 m 2 /g or more. The denitration catalyst is used for denitration at 200° C. or lower.
1. A denitration catalyst obtained by coating a substrate with a catalyst component, wherein the catalyst component contains 80 wt % or more of vanadium pentoxide and has a BET specific surface area of 30 m 2 /g or more, and the denitration catalyst is used for denitration at 200° C. or lower.
2. The denitration catalyst according to claim 1 , wherein in the catalyst component, an amount of NH3 desorbed by NH3-TPD (TPD: temperature programed desorption) is 10.0 μmol/g or more.
3. A method for producing the denitration catalyst according to claim 1 , the method comprising a step of impregnating the substrate with a chelate compound solution in which vanadium pentoxide is dissolved and then performing firing.
4. A method for producing the denitration catalyst according to claim 1 , the method comprising a step of spraying a chelate compound solution in which vanadium pentoxide is dissolved onto the substrate and then performing firing.