Biaxially oriented films made of propylene polymer compositions
The present invention is biaxially oriented film comprising a layer comprising a propylene polymer composition comprising a high isotactic homopolymer of propylene and a polymeric α-nucleating agent. The composition may also comprise other propylene polymers.
1. A biaxially oriented film comprising:
a layer comprising a propylene polymer composition (A) comprising:
(i) from 98.2 to 99.8% by weight of a high isotactic homopolymer of propylene (i) having a content of isotactic pentad fraction of from 93 to 98% and a melt flow rate MFR 2 of from 0.5 to 10 g/10 min; and
(ii) a polymeric α-nucleating agent (ii);
(iii) from 0.1 to 1.0% by weight of a propylene homo- or copolymer (iii) other than (i), the propylene homo- or copolymer (iii) comprising from 0.5 to 50 ppm by weight of the polymeric α-nucleating agent (ii) based on the weight of the propylene homo- or copolymer (iii); and
(iv) from 0.01 to 0.8% by weight of conventional additives (iv), the percentages being based on the weight of the propylene polymer composition (A);
wherein the propylene homopolymer (i) and the propylene homo- or copolymer (iii) do not contain long chain branches and wherein no further polymer containing long chain branches is added to the propylene polymer composition (A).
2. The biaxially oriented film according to claim 1 , wherein the polymeric α-nucleating agent (ii) is selected from the group consisting of polyvinylcyclohexane, poly(3-methyl-1-butene) and mixtures thereof.
3. The biaxially oriented film according to claim 1 , wherein the propylene polymer composition (A) has an ash content of not more than 30 ppm by weight.
4. The biaxially oriented film according to claim 1 , wherein the film comprises a layer consisting of the propylene polymer composition (A).
5. The biaxially oriented film according to claim 1 , wherein the conventional additives (iv) are selected from the antioxidants, stabilisers and acid scavengers.
6. The biaxially oriented film according to claim 1 , wherein the film also comprises a metal layer.
7. The biaxially oriented film according to claim 1 , wherein the thickness of the film is from 1 to 10 μm.
8. A capacitor comprising a film according to claim 1 .
9. The biaxially oriented film according to claim 1 , wherein the propylene homo- or copolymer (iii) comprises from 5 to 50 ppm by weight of the polymeric α-nucleating agent (ii) based on the weight of the propylene homo- or copolymer (iii).