Low permeability and high strength fabric and methods of making the same
An uncoated woven fabric of yarn formed from synthetic fibers woven in the warp direction and weft direction to form a top surface and a bottom surface wherein at least a portion of the yarn on the top surface or at least a portion of the yarn on the bottom surface has fibers with a permanently modified cross-section and that are fused together is provided. Methods for production and use of this fabric in application to products such as automobile airbags, sailcloths, inflatable slides, temporary shelters, tents, ducts, coverings and printed media are also provided.
1. An airbag fabric comprising:
yarn formed from synthetic fibers, with at least a portion of the synthetic fibers on a surface of the yarn are fused while inner synthetic fibers of the yarn are undeformed, the synthetic fibers woven in a warp direction and a weft direction;
wherein the fabric has a static air permeability (SAP) of 3 l/dm 2 /min or lower;
wherein the fabric has a dynamic air permeability (DAP) of 500 mm/s or lower; and
wherein a tensile strength of the fabric in both the warp and weft directions is 1000 N or greater.
2. The airbag fabric of claim 1 , wherein the fabric is uncoated.
3. The airbag fabric of claim 1 , wherein the tensile strength of the fabric in both the warp and weft directions is 2000 N or greater.
4. The airbag fabric of claim 1 , wherein the yarn has a linear density in the range from about 150 to about 750 decitex.
5. The airbag fabric of claim 1 , wherein a basis weight of the fabric is in the range from about 50 to about 500 g/m 2 .
6. The airbag fabric of claim 1 , wherein a tear strength of the fabric in both the warp and weft directions is 60 N or greater.
7. The airbag fabric of claim 1 , wherein an edgecomb resistance of the fabric in both the warp and weft directions is 150 N or greater.
8. The airbag fabric of claim 1 , wherein the fibers have a linear density in the range from about 1 to about 25 decitex.
9. The airbag fabric of claim 1 , wherein the fibers are formed from a polymer selected from the group consisting of polyamides, polyesters, polyolefins and blends or copolymers thereof.
10. The airbag fabric of claim 1 , wherein the fabric has a dynamic air permeability (DAP) of 400 mm/s or lower.
11. The airbag fabric of claim 1 , wherein all of the yarn used in the warp and weft directions is formed from a single polymer or a blend of polymers.
12. The airbag fabric of claim 1 , wherein at least a portion of the fibers are substantially flat.