Method for manufacturing electrode
The present disclosure is intended to solve non-uniform distribution of a polymer binder in an electrode active material layer and to improve the adhesion between an electrode current collector and an electrode active material layer. The present disclosure provides a method for manufacturing an electrode which includes the steps of: (S1) applying electrode slurry containing an electrode active material, a polymer binder and a conductive material dispersed in a solvent to one surface of an electrode current collector; (S2) stacking a polymer film onto the top surface coated with the electrode slurry; (S3) drying the electrode current collector having the polymer film stacked thereon to allow evaporation of the solvent; and (S4) rolling the electrode current collector having the polymer film stacked thereon to obtain an electrode.
1. A method for manufacturing an electrode which comprises the steps of:
(S1) applying electrode slurry containing an electrode active material, a polymer binder and a conductive material dispersed in a solvent to one surface of an electrode current collector;
(S2) stacking a polymer film onto the top surface coated with the electrode slurry;
(S3) drying the electrode current collector having the polymer film stacked thereon to allow evaporation of the solvent wherein the evaporation is to the lateral sides of the electrode;
(S4) rolling the electrode current collector having the polymer film stacked thereon to obtain an electrode; and
(S5) removing the polymer film.
2. The method for manufacturing an electrode according to claim 1 , wherein the polymer film is a polymethyl methacrylate, polydimethylsiloxane or a plastic paraffin film.
3. The method for manufacturing an electrode according to claim 1 , wherein the electrode current collector is a porous electrode current collector.
4. The method for manufacturing an electrode according to claim 3 , wherein the pores of the porous electrode current collector have a diameter of 1-20 μm.
5. The method for manufacturing an electrode according to claim 1 , wherein the polymer film has a thickness of 100-2000 μm.