Method of and system for building up a dental object
A method of building up a dental object includes steps of (i) determining the three-dimensional shape of the object; (ii) mixing at least a first and a second component to form a hardenable composition; (iii) depositing the hardenable composition through a nozzle; (iv) performing steps (ii) and (iii) in combination with moving the nozzle by computer control based on said data. The invention helps providing an object like a dental restoration at maximized geometric and optical quality.
1. A method of building up a dental object, comprising:
(i) determining a three-dimensional shape of the dental object in the form of computer-processible data which represents the three-dimensional shape;
(ii) providing a first component, a second component, and a third component,
(iii) mixing the first component, the second component, and the third component to form a hardenable composition,
the first component comprising a light-polymerizable composition and a photoinitiator,
the second component comprising a coloring agent, and
the third component comprising a coloring agent,
wherein at least one combination of the first component, the second component, and third component are mixed at a variable ratio for a period while continuously dispensing;
(iv) depositing the hardenable composition through a nozzle; and
(v) performing steps (iii) and (iv) in combination with moving the nozzle by computer control based on the computer-processible data to build up the dental object by incremental depositing the hardenable composition,
wherein the mixing of the first component, the second component, and the third component is effective in providing color-graded hardened composition.
2. The method of claim 1 , wherein the hardenable composition is selected and wherein the steps (iii) and (iv) are performed so that the hardenable composition is not yet fully hardened in step (iv).
3. The method of claim 1 , wherein the second component and the third component are configured to provide the color-graded hardened composition with different physical properties, selected from different colorings, different hardnesses, different E-modules, different translucencies, and a combination thereof.
4. The method of claim 3 , wherein the first component, the second component and the third component are supplied at a first flow rate A, a second flow rate B and a third flow rate C, respectively, the second flow rate B and the third flow rate C and together are defined by a common flow rate D,
wherein the common flow rate D is constant, and
wherein a mixing ratio of flow rate A:flow rate D is constant.
5. The method of claim 4 , wherein a ratio of flow rate B:flow rate C is variable.
6. The method of claim 1 , wherein the hardenable composition is a dental composition.
7. The method of claim 6 , wherein the dental object is in a shape of a dental restoration or an orthodontic bracket.
8. The method of claim 6 , wherein the dental object is a dental blank.
9. The method of claim 1 , further comprising:
providing a geometrically predetermined support structure;
depositing the hardenable composition directly onto the support structure to form a dental blank;
using the support structure to receive the dental blank in a receptacle of a milling or grinding machine; and
machining by aid of the milling or grinding machine a dental object from the dental blank.
10. The method of claim 1 , further comprising the step of exposing the hardenable composition to excitation for modifying the viscosity during depositing.
11. The method of claim 1 , further comprising irradiating increments of a deposited hardenable composition.