High flow TPO composition with excellent balance in mechanical properties for automotive interior

1. A heterophasic propylene copolymer (HECO) comprising:

a) a propylene homopolymer (HPP) having a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 100 to 200 g/10 min, and

b) an elastomeric propylene-ethylene copolymer (E), wherein the heterophasic propylene copolymer (HECO)

(i) has a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 15 to 35 g/10 min,

(ii) comprises a xylene cold soluble (XCS) fraction in an amount from 26 to 36 wt. %, based on the total weight of the heterophasic propylene copolymer (HECO),wherein further the xylene cold soluble (XCS) fraction of the heterophasic propylene copolymer (HECO) has

(iii) an intrinsic viscosity (IV) measured according to DIN ISO 1628/1 in the range of 2.8 to 3.8 dl/g, and

(iv) an ethylene content (EC) of 35 to 50 wt. % based on the total weight of the xylene cold soluble (XCS) fraction of the heterophasic propylene copolymer (HECO), and

wherein xylene cold soluble (XCS) fraction is unimodal with respect to the ethylene content (EC) and/or unimodal with respect to the molecular weight distribution (MWD).

2. The heterophasic propylene copolymer (HECO) according to claim 1 , wherein the propylene homopolymer (HPP) is unimodal with respect to the melt flow rate MFR 2 (230° C.) measured according to ISO 1133 and/or has a xylene cold soluble (XCS) content no higher than 5 wt. %.

3. The heterophasic propylene copolymer (HECO) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) has an ethylene content (EC-HECO) of 8 to 18 wt. %, based on the total weight of the heterophasic propylene copolymer (HECO).

4. The heterophasic propylene copolymer (HECO) according to claim 1 , wherein the weight ratio of heterophasic propylene copolymer (HECO) to the polypropylene homopolymer (HPP) [HECO/HPP] is from 3.0:1.0 to 1.0:1.0.

5. The heterophasic propylene copolymer (HECO) according to claim 1 , wherein the heterophasic propylene copolymer (HECO) is α-nucleated.

6. A polyolefin composition (PO) comprising ≥95 wt. %, based on the total weight of the composition, of the heterophasic propylene copolymer (HECO) according to claim 1 .

7. The polyolefin composition (PO) according to claim 6 , wherein the composition comprises an inorganic filler (F) selected from the group consisting of talc, wollastonite, mica, chalk and mixtures thereof.

8. The polyolefin composition (PO) according to claim 6 , wherein the composition has:

i) a melt flow rate MFR 2 (230° C.) measured according to ISO 1133 in the range of 15 to 35 g/10 min, and

ii) a tensile modulus of ≥850 MPa measured according to ISO 527-2, and/or

iii) a Charpy Notched impact strength at 23° C. of ≥+kJ/m 2 measured according to ISO 179-1/1 eA.

9. The polyolefin composition (PO) according to claim 8 , wherein the composition has:

i) a tensile modulus in the range of 850 to 1250 MPa measured according to ISO 527-2, and/or

ii) a Charpy Notched impact strength at 23° C. in the range of 30 to 60 kJ/m 2 measured according to ISO 179-1/1 eA.

10. An automotive article comprising the heterophasic propylene copolymer (HECO) according to claim 1 .

11. The automotive article according to claim 10 , wherein the automotive article is an exterior or interior automotive article selected from bumpers, body panels, rocker panels, side trim panels, interior trims, step assists, spoilers, fenders and dash boards.