SURFACE COVERING HAVING AN IMPROVED WEAR LAYER
Described herein is a floor covering comprising: a substrate, and a coating layer comprising a cross-linked polymer formed from a curable coating composition comprising an acrylate-functional resin; wherein the cross-linked polymer has a glass transition temperature equal to or greater than room temperature and has a cross-link density of at least about 0.0035 C═C eq/gm as measured from the polymerization of carbon-carbon double bonds in the curable coating composition.
1 . A floor covering comprising:
a substrate, and
a coating layer comprising a cross-linked polymer formed from a curable coating composition comprising an acrylate-functional resin;
wherein the cross-linked polymer has a glass transition temperature equal to or greater than room temperature and has a cross-link density of at least about 0.0035 C═C eq/gm as measured from the polymerization of carbon-carbon double bonds in the curable coating composition.
2 . The floor covering of claim 1 , wherein the cross-link density is at least about 0.004 C═C eq/gm.
3 . The floor covering of claim 1 , wherein the glass transition temperature of the cross-linked polymer is at least about 40° C.
4 . The floor covering of claim 1 , wherein the acrylate-functional resin comprises acrylate-functional polymeric resin is selected from polyester acrylate resin, urethane acrylate resin, and a combination thereof.
5 . The floor covering of claim 4 , wherein acrylate-functional resin further comprises a mixture of a first acrylate oligomer having an acrylate functionality of two and a second acrylate oligomer having an acrylate functionality of three, the first acrylate oligomer and the second acrylate oligomer are present in the curable coating composition in a weight ratio ranging from about 2:1 to about 6:1.
6 . The floor covering of claim 5 , wherein the acrylate-functional polymeric resin and the second acrylate oligomer are present in the curable coating composition in a weight ratio ranging from about 7:1 to about 11:1.
5 . The floor covering of claim 5 wherein the first acrylate oligomer is selected from ethylene glycol diacrylate, propylene glycol diacrylate, diethylene glycol diacrylate, dipropylene glycol diacrylate, triethylene glycol diacrylate, tripropylene glycol diacrylate, polyethylene glycol diacrylate, polypropylene glycol diacrylate, ethoxylated bisphenol A diacrylate, bisphenol A diglycidyl ether diacrylate, resorcinol diglycidyl ether diacrylate, 1,3-propanediol diacrylate, 1,4-butanediol diacrylate, 1,5-pentanediol diacrylate, 1,6-hexanediol diacrylate, neopentyl glycol diacrylate, cyclohexane dimethanol diacrylate, ethoxylated neopentyl glycol diacrylate, propoxylated neopentyl glycol diacrylate, ethoxylated cyclohexanedimethanol diacrylate, propoxylated cyclohexanedimethanol diacrylate, and mixtures thereof.
6 . The floor covering of claim 5 wherein the second acrylate oligomer is selected from trimethylol propane triacrylate, isocyanurate triacrylate, glycerol triacrylate, ethoxylated trimethylolpropane triacrylate, propoxylated trimethylolpropane triacrylate, tris (2-hydroxyethyl) isocyanurate triacrylate, ethoxylated glycerol triacrylate, propoxylated glycerol triacrylate, pentaerythritol triacrylate, melamine triacrylates, and mixtures thereof.
7 . The floor covering of claim 1 wherein the curable coating composition further comprises a third oligomer having an acrylate functionality of three.
8 . The floor covering of claim 7 wherein the third oligomer is selected from di-trimethylolpropane tetraacrylate, pentaerythritol tetraacrylate, ethoxylated pentaerythritol tetraacrylate, propoxylated pentaerythritol tetraacrylate, di-pentaerythritol tetraacrylate, ethoxylated dipentaerythritol tetraacrylate, propoxylated dipentaerythritol tetraacrylate, and combinations thereof.
9 . The floor covering of claim 1 wherein the coating layer has an average thickness ranging from about 2 μm to about 50 μm.
10 . The floor covering of claim 1 wherein the curable coating composition is substantially free of fluoro-carbon compounds.
11 . The floor covering of claim 1 wherein the curable coating composition is substantially free of siloxane compounds.
12 . The floor covering of claim 1 , wherein the substrate is a vinyl tile.
13 . A floor covering comprising:
a substrate, and
a coating layer comprising a cross-linked polymer formed from a curable coating composition comprising a mixture of:
an acrylate-functional polymeric resin;
an acrylate-functional oligomer having an acrylate-functionality ranging from two to four;
wherein the cross-linked polymer has a glass transition temperature of at least about 40° C. and has a cross-link density of at least about 0.004 C═C eq/gm as measured from the polymerization of carbon-carbon double bonds in the curable coating composition.
14 . The floor covering of claim 13 , wherein the glass transition temperature of the cross-linked polymer is at least about 45° C.
15 . The floor covering of claim 1 , wherein the acrylate-functional polymeric resin is selected from polyester acrylate resin, urethane acrylate resin, and a combination thereof.
16 . The floor covering of claim 1 , wherein the acrylate-functional oligomer comprises a first acrylate oligomer having an acrylate functionality of two and a second acrylate oligomer having an acrylate functionality of three; wherein the first acrylate oligomer and the second acrylate oligomer are present in the curable coating composition in a weight ratio ranging from about 2:1 to about 5:1.
17 . The floor covering of claim 1 , wherein acrylate-functional oligomer further comprises a third acrylate having an acrylate functionality of four, and the first acrylate oligomer and the third acrylate oligomer are present in the curable coating composition in a weight ratio ranging from about 4:1 to about 6:1.
18 . The floor covering of claim 16 , wherein the first acrylate oligomer and the acrylate-functional polymeric resin are present in the curable coating composition in a weight ratio ranging from about 0.5:1 to about 2:1.
19 . The floor covering of claim 1 , wherein the substrate is a vinyl tile.
20 . A method of forming a floor covering comprising:
mixing together an acrylate polymeric resin, a di-functional acrylate oligomer, and a tri-functional acrylate oligomer to form a curable coating composition;
applying the curable coating composition to a top surface of a substrate; and
exposing the curable coating composition to form a cross-linked coating layer;
wherein the cross-linked coating layer has a glass transition temperature of at least about 30° C. and has a cross-link density of at least about 0.0035 C═C eq/gm as measured from the polymerization of carbon-carbon double bonds in the curable coating composition.