Polarizer protective film, polarizing plate, and display device comprising same
Embodiments relate to a protective film for a polarizer, a polarizing plate, and a display device comprising the same. The protective film for a polarizer according to the embodiments is improved in mechanical strength and minimized in rainbow strains by minimizing the difference in the orientation angle between the center and the edge of the film while generating a difference in the strengths in the longitudinal/transverse directions of the film. Hence, it can be advantageously used as a protective film for a polarizer.
1. A protective film for polarizer, which is a biaxially stretched polyester film having a stretch ratio in transverse direction (TD) of 4.15 or more and a stretch ratio in longitudinal direction (MD) of 1.2 to 2.0,
which has a tensile strength in the longitudinal direction of 9.0 to 18 kgf/mm 2 , a tensile strength in the transverse direction of 24 to 35 kgf/mm 2 , a ratio of the tensile strength in the longitudinal direction (MD) to the tensile strength in the transverse direction (TD) of 0.25 to 0.35, and an in-plane retardation of 3,000 nm or more,
wherein the protective film has a modulus in the longitudinal direction (MD) of 225 kgf/mm 2 to 290 kgf/mm 2 and a modulus in the transverse direction (TD) of 480 kgf/mm 2 to 560 kgf/mm 2 , a ratio of the modulus in the longitudinal direction (MD) to the modulus in the transverse direction (TD) of 0.4 to 0.6,
wherein the protective film has a deviation in the orientation angle of ±2.5 degrees or less in its entire width, and
wherein the protective film shows a change in the in-plane retardation by less than 400 nm across the width of the film.
2. The protective film for polarizer of claim 1 , wherein the in-plane retardation is 7,500 nm or more.
3. A polarizing plate, which comprises:
a polarizer layer; and
a protective film for polarizer adjacent to at least one of the upper and lower sides of the polarizer layer,
wherein the protective film for polarizer is a biaxially stretched polyester film having a stretch ratio in transverse direction (TD) of 4.15 or more and a stretch ratio in longitudinal direction (MD) of 1.2 to 2.0,
wherein the protective film for polarizer has a tensile strength in the longitudinal direction (MD) of 9.0 to 18 kgf/mm 2 , a tensile strength in the transverse direction (TD) of 24 to 35 kgf/mm 2 , a ratio of the tensile strength in the longitudinal direction (MD) to the tensile strength in the transverse direction (TD) of 0.25 to 0.35, and an in-plane retardation of 3,000 nm or more,
wherein the protective film for polarizer has a modulus in the longitudinal direction (MD) of 225 kgf/mm 2 to 290 kgf/mm 2 and a modulus in the transverse direction (TD) of 480 kgf/mm 2 to 560 kgf/mm 2 , a ratio of the modulus in the longitudinal direction (MD) to the modulus in the transverse direction (TD) of 0.4 to 0.6,
wherein the protective film for polarizer has a deviation in the orientation angle of ±2.5 degrees or less in its entire width, and
wherein the protective film for polarizer shows a change in the in-plane retardation by less than 400 nm across the width of the film.
4. The polarizing plate of claim 3 , wherein the protective film shows a change in the in-plane retardation by less than 400 nm across the width of the protective film.
5. The polarizing plate of claim 3 , wherein the protective film has a ratio of the tensile strength in the longitudinal direction (MD) to the tensile strength in the transverse direction (TD) of 0.25 to 0.4.
6. The polarizing plate of claim 5 , wherein the film has an in-plane retardation of 7,500 nm or more.
7. A display device, which comprises:
a display panel; and
a polarizing plate disposed on at least one of the upper and lower sides of the display panel,
wherein the polarizing plate comprises a polarizer layer; and a protective film for a polarizer adjacent to at least one of the upper and lower sides of the polarizer layer,
wherein the protective film for polarizer is a biaxially stretched polyester film having a stretch ratio in transverse direction (TD) of 4.15 times or more and a stretch ratio in longitudinal direction (MD) of 1.2 to 2.0,
the protective film for polarizer has a tensile strength in the longitudinal direction (MD) of 9.0 to 18 kgf/mm 2 , a tensile strength in the transverse direction (TD) of 24 to 35 kgf/mm 2 , a ratio of the tensile strength in the longitudinal direction (MD) to the tensile strength in the transverse direction (TD) of 0.25 to 0.35, and an in-plane retardation of 3,000 nm or more,
wherein the protective film for polarizer has a modulus in the longitudinal direction (MD) of 225 kgf/mm 2 to 290 kgf/mm 2 and a modulus in the transverse direction (TD) of 480 kgf/mm 2 to 560 kgf/mm 2 , a ratio of the modulus in the longitudinal direction (MD) to the modulus in the transverse direction (TD) of 0.4 to 0.6,
wherein the protective film for polarizer has a deviation in the orientation angle of ±2.5 degrees or less in its entire width, and
wherein the protective film for polarizer shows a change in the in-plane retardation by less than 400 nm across the width of the film.
8. A process for preparing a protective film for polarizer according to claim 1 , which comprises:
casting a polyester resin to produce an unstretched sheet;
stretching the unstretched sheet by 1.2 to 2.0 times in its longitudinal direction (MD) or stretching the unstretched sheet by 4.15 times or more in its transverse direction (TD) to give an uniaxially stretched polyester film in either longitudinal direction (MD) or transverse direction (TD); and
stretching the uniaxially stretched polyester film in the other direction to give biaxially stretched polyester film in both longitudinal direction (MD) and transverse direction (TD),
wherein the biaxially stretched film has a tensile strength in the longitudinal direction (MD) of 9.0 to 18 kgf/mm 2 , a tensile strength in the transverse direction (TD) of 24 to 35 kgf/mm 2 , a ratio of the tensile strength in the longitudinal direction (MD) to the tensile strength in the transverse direction (TD) of 0.25 to 0.35, an in-plane retardation of 3,000 nm or more;
wherein the biaxially stretched film has a modulus in the longitudinal direction (MD) of 225 kgf/mm 2 to 290 kgf/mm 2 and a modulus in the transverse direction (TD) of 480 kgf/mm 2 to 560 kgf/mm 2 ; a ratio of the modulus in the longitudinal direction to the modulus in the transverse direction of 0.4 to 0.6; and a deviation in the orientation angle of ±2.5 degrees or less in its entire width, and
wherein the protective film for polarizer shows a change in the in-plane retardation by less than 400 nm across the width of the protective film.
9. The process for preparing a protective film for polarizer of claim 8 , which further comprises heat setting the biaxially stretched film,
wherein temperature of the heat setting is 200° C. to 210° C., and
duration of the heat setting is 6 seconds to 13 seconds.
10. The process for preparing a protective film for polarizer of claim 8 , wherein in the stretching step in the transverse direction (TD), the stretching speed in the transverse direction (TD) is 350%/min to 800%/min.