Glass-fiber-reinforced polyamide resin composition
The present invention is a glass-fiber-reinforced polyamide resin composition which contains a crystalline aliphatic polyamide resin (A), an amorphous polyamide resin (B), an acrylic resin (C), mica (D), glass fiber (E) and carbon black (F) in a ratio by mass of (10 to 40):(2 to 20):(1 to 10):(2 to 25):(20 to 50):(0.1 to 5), respectively and further contains a copper compound (G) in a rate of 0.005 to 1.0 part by mass when a total amount of the ingredients (A) to (F) is taken as 100 parts by mass.
1. A glass-fiber-reinforced polyamide resin composition, comprising a crystalline aliphatic polyamide resin (A), an amorphous polyamide resin (B), poly(methyl methacrylate) (C), mica (D), glass fiber (E) and a carbon black master batch (F) in a ratio by mass of (20 to 30):(10 to 15):(2 to 6):(15 to 22):(25 to 45):(1 to 4.5), respectively, and further comprising a copper compound (G) in a ratio of 0.005 to 1.0 part by mass when a total amount of the ingredients (A) to (F) is taken as 100 parts by mass,
wherein, when a flat plate is prepared by subjecting the glass-fiber-reinforced polyamide resin composition to an injection molding and the resulting plate is subjected to a weathering test in accordance with JIS K 7350-2, a color difference ΔE before and after the weathering test is 3.5 or less.
2. The glass-fiber-reinforced polyamide resin composition according to claim 1 , wherein the amorphous polyamide resin (B) is a semi-aromatic polyamide.
3. The glass-fiber-reinforced polyamide resin composition according to claim 1 , comprising the crystalline aliphatic polyamide resin (A), the amorphous polyamide resin (B), the poly(methyl methacrylate) (C), the mica (D), the glass fiber (E) and the carbon black master batch (F) in a ratio by mass of (21.5 to 24):(11.5 to 14.5):(2 to 6):(16 to 20):(35 to 41):(1 to 4.5), respectively, and further comprising the copper compound (G) in a ratio of 0.02 to 0.3 part by mass when the total amount of the ingredients (A) to (F) is taken as 100 parts by mass, and
wherein the color difference ΔE before and after the weathering test is 3.3 or less.
4. A molded product for vehicle interior or vehicle exterior, wherein the molded product is molded from the glass-fiber-reinforced polyamide resin composition according to claim 1 .
5. The molded product for vehicle interior or vehicle exterior according to claim 4 , wherein the product is selected from the group consisting of an outer handle, an outer door handle, a wheel cap, a roof rail, a door mirror base, a room mirror arm, a sunroof deflector, a radiator fan, a radiator grill, a bearing retainer, a console box, a sun visor arm, a spoiler and a slide door rail cover.