EXTRUDED ARTICLES WITH IMPROVED OPTICAL PROPERTIES
Extruded articles based on a nucleated polypropylene homopolymer showing improved optical properties such as haze or relative haze and a good balance between optical and thermomechanical properties.
1 . An extruded article comprising a polypropylene homopolymer, wherein the polypropylene homopolymer is polymerised in the presence of a Ziegler-Natta catalyst wherein the polypropylene homopolymer;
a. has a MFR230/2.16 according to ISO1133 in the range of 1-200 g/10 min,
b. is free of phthalic acid esters as well as their respective decomposition products,
c. comprises at least one α-nucleating agent,
d. comprises 0-1.0 wt. % of ethylene and/or a C 4 -C 10 α-olefin, and
e. the extruded article has a relative haze of 0.165%/μm or below,
wherein the Ziegler-Natta-Catalyst comprises:
a. compounds of a transition metal of Group 4 to 6 of IUPAC,
b. a Group 2 metal compound,
c. an internal donor, wherein said internal donor is a non-phthalic compound,
d. a co-catalyst, and
e. optionally an external donor.
2 . The extruded article according to claim 1 , wherein the at least one α-nucleating agent is a polymeric nucleating agent and/or a mono- or poly-carboxylic acid nucleating agent.
3 . The extruded article according to claim 1 , wherein the polypropylene homopolymer comprises 0-0. 40 wt. % of ethylene and/or a C 4 -C 10 α-olefin.
4 . The extruded article according to claim 3 , wherein the extruded article comprises a haze according to ASTM 1003 of 8.3% when measured on 50 μm cast film.
5 . The extruded article according to claim 3 , wherein the polypropylene homopolymer comprises a polymeric nucleating agent.
6 . The extruded article according to claim 1 , wherein the polypropylene homopolymer comprises >0.40-0.90 wt. % of ethylene and/or a C 4 -C 10 α-olefin.
7 . The extruded article according to according to claim 1 , comprising:
a. a relative haze of 0.120%/μm or below,
b. a shrinkage determined at 165° C. of (−10)% or higher, or
c. a gloss-in according to ISO2813 of at least 122.5%.
8 . The extruded article according to claim 7 , wherein the polypropylene homopolymer comprises a mono-or poly-carboxylic acid nucleating agent.
9 . The extruded article according to claim 6 , wherein the extruded article comprises a haze of 12.0% when measured on a 300 μm sheet.
10 . The extruded article according to claim 1 , wherein the extruded article has a wall thickness of 2000 μm or below.
11 . The extruded article according to claim 1 , wherein the article is a blown film, a cast film, a sheet or a layer of a multilayer film or multilayer sheet.
12 . Final articles comprising the extruded article according to claim 1 .
13 . A method for producing an extruded article according to claim 1 , with improved optical properties including haze or relative haze, comprising the steps of:
a. polymerising propylene and optionally ethylene in the presence of a Ziegler-Natta catalyst, wherein the Ziegler-Natta-catalyst comprises:
i. compounds of a transition metal of Group 4 to 6 of IUPAC,
ii. a Group 2 metal compound (MC),
iii. an internal donor (ID), wherein said internal donor (ID) is a non-phthalic compound,
iv. a co-catalyst (Co), and
v. optionally an external donor (ED)
b. incorporating at least one α-nucleating agent
c. extruding articles comprising said polymer obtained in step a) to b).
14 . (canceled)