Waterborne latex coating compositions with viscosity-modifying coalescence aids
A coating composition including about 5 wt % to about 70 wt % of a latex or a water-dispersible film forming polymer, based on the total weight of the coating composition, a surfactant present in the coating composition at 0.1% to about 1% on the continuous phase of the coating composition; a polymeric associative thickener present in the coating composition at about 0.1% to about 2% on the continuous phase of the coating composition; about 0.1 wt % to about 5 wt % a styrene acrylic resin, based on the total weight of the coating composition; and an aqueous diluent.
1. A coating composition, comprising:
about 5 wt % to about 70 wt % of a latex or a water-dispersible film forming polymer, based on the total weight of the coating composition;
a surfactant present in the coating composition at 0.1% to about 1% on the continuous phase of the coating composition;
a polymeric associative thickener present in the coating composition at about 0.1% to about 2% on the continuous phase of the coating composition;
about 0.1 wt % to about 1.5 wt % of a styrene acrylic resin, based on the total weight of the coating composition; and
an aqueous diluent.
2. The composition of claim 1 , wherein the polymeric associative thickener is chosen from HEUR thickeners, HASE thickeners, and combinations thereof.
3. The composition of claim 2 , wherein the polymeric associate thickener is a HEUR thickener.
4. The composition of claim 3 , wherein the HEUR thickener comprises a backbone comprising poly(ethylene glycol) (PEG) or diisocyanate.
5. The composition of claim 4 , wherein the HEUR thickener comprises end caps on the backbone, and wherein the end caps are chosen from hydrophobic alcohols, hydrophobic amines, and combinations thereof.
6. The composition of claim 5 , wherein the HEUR thickener has a molecular weight of about 15,000 to about 100,000.
7. The composition of claim 1 , wherein the styrene acrylic resin has a VOC concentration of less than about 50%.
8. The composition of claim 1 , wherein the film forming polymer comprises a (meth)acrylic polymer.
9. The composition of claim 1 , wherein the surfactant comprises at least one of nonionic octylphenol ethoxylates and sodium dodecyl sulfate.
10. The composition of claim 1 , wherein the aqueous diluent comprises a cosolvent.
11. The composition of claim 1 , wherein the coating composition further comprises a colorant.
12. The composition of claim 11 , wherein the colorant comprises a pigment.
13. A coated component comprising a substrate having thereon a wet coating, the coating comprising:
about 5 wt % to about 70 wt % of a latex or a water-dispersible film forming polymer, based on the total weight of the coating composition;
a surfactant present in the coating composition at 0.1% to about 1% on the continuous phase of the coating composition;
a polymeric associative HEUR thickener present in the coating composition at about 0.1% to about 2% on the continuous phase of the coating composition;
about 0.1 wt % to about 1.5 wt % of a low-VOC styrene acrylic resin, based on the total weight of the coating composition;
an aqueous diluent; and
a pigment.
14. The component of claim 13 , wherein the HEUR thickener has backbone comprising poly(ethylene glycol) (PEG) or diisocyanate and end caps on the backbone, and wherein the end caps are chosen from hydrophobic alcohols, hydrophobic amines, and combinations thereof.
15. The component of claim 13 , wherein the HEUR thickener has a molecular weight of about 15,000 to about 100,000.
16. The component of claim 13 , wherein the film forming polymer comprises a (meth)acrylic polymer.
17. The component of claim 13 , wherein the surfactant comprises at least one of nonionic octylphenol ethoxylates and sodium dodecyl sulfate.
18. A method for coating a component, comprising:
applying to a substrate a wet coating composition comprising:
about 5 wt % to about 70 wt % of a latex or a water-dispersible film forming polymer, based on the total weight of the coating composition;
a surfactant present in the coating composition at 0.1% to about 1% on the continuous phase of the coating composition;
a polymeric associative HEUR thickener present in the coating composition at about 0.1% to about 2% on the continuous phase of the coating composition;
about 0.1 wt % to about 1.5 wt % of a low-VOC styrene acrylic resin, based on the total weight of the coating composition;
an aqueous diluent; and
a pigment; and
curing the wet coating composition to form a coating on the substrate.