Near-infrared cut filter glass
A near-infrared cut filter glass includes: P, Al, R (R represents any one or more of Li, Na, and K), R′ (R′ represents any one or more of Mg, Ca, Sr, Ba, and Zn), and Cu, and not including F practically, wherein (Cu + amount/total Cu amount)×100[%] is 0.01 to 7.0%. The filter glass may further include, by mol %, 0 to 10% B 2 O 3 . The filter glass may have a fracture toughness value of the near-infrared cut filter glass is 0.3 MPa·m 1/2 or more. For the filter glass, a quotient obtained by dividing an absorption constant at a wavelength of 430 nm by an absorption constant at a wavelength of 800 nm, of the near-infrared cut filter glass, may be 0.00001 to 0.19.
1. A near-infrared cut filter glass comprising: P, Al, R, R′, and Cu, and not comprising F practically, wherein
R represents any one or more of Li, Na, and K;
R′ represents any one or more of Mg, Ca, Sr, Ba, and Zn; and
(Cu + weight % amount/total Cu weight % amount)×100[%] is 0.01 to 5.0%, wherein the near-infrared cut filter glass comprises, by mol %:
50 to 75% P 2 O 5 ;
5 to 22% Al 2 O 3 ;
0.5 to 20% R 2 O, wherein 0.5 to 15% is K 2 O;
0.1 to 20% R′O; and
0.1 to 15% CuO.
2. The near-infrared cut filter glass according to claim 1 , comprising, by mol %, 0 to 10% B 2 O 3 .
3. The near-infrared cut filter glass according to claim 1 , comprising, by mol %, greater than 0 to 10% B 2 O 3 .
4. The near-infrared cut filter glass according to claim 1 , comprising, by mol %, 2.3 to 10% B 2 O 3 .
5. The near-infrared cut filter glass according to claim 1 , comprising, by mol %, 52 to 75% P 2 O 5 .
6. The near-infrared cut filter glass according to claim 1 , comprising, by mol %, 1.6 to 10% K 2 O.
7. The near-infrared cut filter glass according to claim 1 , wherein the (Cu + weight % amount/total Cu weight % amount)×100[%] is 0.01 to 4.5%.
8. The near-infrared cut filter glass according to claim 1 , wherein the (Cu + weight % amount/total Cu weight % amount)×100[%] is 0.05 to 4.5%.
9. The near-infrared cut filter glass according to claim 1 , wherein a fracture toughness value of the near-infrared cut filter glass is 0.3 MPa·m 1/2 or more.
10. The near-infrared cut filter glass according to claim 1 , wherein a quotient obtained by dividing an absorption constant at a wavelength of 430 nm by an absorption constant at a wavelength of 800 nm, of the near-infrared cut filter glass, is 0.00001 to 0.19.
11. The near-infrared cut filter glass according to claim 1 , wherein a transmittance at a wavelength of 430 nm at a thickness of 0.3 mm of the near-infrared cut filter glass is 50 to 92%.
12. The near-infrared cut filter glass according to claim 11 , wherein the transmittance at a wavelength of 430 nm at a thickness of 0.3 mm of the near-infrared cut filter glass is 84.7 to 92%.