Mesoporous surface for enhanced bone integration
Techniques for creating a mesoporous surface for enhanced bone integration are provided. An example of a method for generating a mesoporous surface on a substrate includes depositing a layer of titanium on an area of the substrate to generate a nano-textured surface, and anodizing the layer of titanium on the area of the substrate to generate the mesoporous surface. The method may also include incorporating pharmaceutical, biological, or molecular additives into the mesoporous surface intended to further enhance performance of the substrate via enhanced osseoconduction, osseoinduction, or antimicrobial/anti-infective properties.
1. A method for generating a mesoporous surface on a substrate, comprising:
grit-blasting an area of the substrate to generate a macro-textured surface;
depositing a layer of titanium on the area of the substrate to generate a nano-textured surface; and
anodizing the layer of titanium on the area of the substrate to generate the mesoporous surface.
2. The method of claim 1 wherein the substrate comprises a polyetheretherketone (PEEK) material.
3. The method of claim 1 wherein grit-blasting the area of the substrate includes air-blasting the area with 50-100 μm in diameter micro-beads of SiO 2 or Al 2 O 3 .
4. The method of claim 1 further comprising incorporating pharmaceutical, biological, or molecular additives into the mesoporous surface intended to further enhance performance of the substrate via enhanced osseoconduction, osseoinduction, or antimicrobial/anti-infective properties.
5. The method of claim 1 comprising depositing the layer of titanium on the area of the substrate with an ion beam assisted deposition (IBAD) process.
6. The method of claim 5 wherein the IBAD process utilizes an ion beam energy between 50 eV and 5000 eV.
7. The method of claim 1 wherein the layer of titanium is between 0.5 μm to 10 μm thick.
8. The method of claim 1 wherein anodizing the layer of titanium on the area of the substrate includes an electrochemical oxidation process in a hydrofluoric (HF) acid-based solution.
9. The method of claim 1 wherein anodizing the layer of titanium on the area of the substrate includes an electrochemical oxidation process in an ammonium fluoride (NH 4 F) acid-based solution.
10. The method of claim 1 wherein anodizing the layer of titanium on the area of the substrate includes an electrochemical oxidation process in a solution of nitric acid, hydrochloric acid, acetic acid, trichloroacetic acid, phosphoric acid, sulfuric acid, potassium hydroxide, sodium hydroxide, or combinations thereof.
11. The method of claim 1 wherein the mesoporous surface comprises pore sizes of between 1-50 nanometers in a lateral dimension and between 10-500 nanometers in depth.