Polyethylene composition and process for polymerizing the same
The instant invention provides a polyethylene composition and process for polymerizing the same. The polyethylene composition according to the present invention comprises the polymerization reaction of ethylene and optionally one or more α-olefin comonomers in the presence of a catalyst system, wherein said polyethylene composition comprises at least 2 or more molecular weight distributions, measured via triple detector GPC low angle laser light scattering (GPC-LALLS), described in further details hereinbelow, wherein each molecular weight distribution has a peak, and wherein measured detector response of peak 1 divided by the measured detector response of peak 2 is in the range of from 0.50 to 0.79, for example from 0.55 to 0.77.
1. A process for polymerizing a polyethylene composition comprising the steps of:
(A) Preparing a slurry of a precursor and a viscous inert liquid, said slurry having a viscosity of at least 500 cp, the precursor a formula MgdMe(OR)eXf(ED)g, wherein R is an aliphatic or aromatic hydrocarbon radical having 1 to 14 carbon atoms or COR′ wherein R′ is a aliphatic or aromatic hydrocarbon radical having 1 to 14 carbon atoms, each OR group is the same or different; X is independently chlorine, bromine, or iodine; ED is an electron donor chosen from an organic Lewis base; d is 0.5 to 56; e is 0, 1, or 2; f is 2 to 116 and g is >1 to 20; Me is a transition metal selected from the group of titanium, zirconium, hafnium, and vanadium;
(B) Contacting the slurry of (A.) with a first Lewis Acid such that at least a portion of the organic Lewis Base is complexed with the first Lewis Acid wherein the first Lewis Acid has the formula MRnX(m−n), M is Al, B or Si, R is a C1 to C14 alkyl or aryl radical, X is C1, Br or I, m+n satisfies the valency of the metal M, n is 0 to 3;
(C) Contacting the slurry of (B) with a second different Lewis Acid with the formula MRnX(m−n), M is A1, or B, R is a C1 to C14 alkyl or aryl radical, X is Cl, Br or I, m+n satisfies the valency of the metal M, n is 0 to 2; (D) Feeding the slurry of (C) into a gas phase reactor in which an olefin polymerization reaction is in progress in the presence of one or more cocatalysts and wherein the molar ratios of the first Lewis Acid and second different Lewis Acid to the electron donor are controlled to affect specific fractions of the molecular weight distribution of the final polymer product;
(E) Where both the relative ratio of the first Lewis Acid and second different Lewis Acid to electron donor and the chemical identity of the first Lewis Acid and second different Lewis Acid is adjusted to polymerize said polyethylene composition, wherein said polyethylene composition comprises at least 2 molecular weight distributions, measured via triple detector GPC low angle laser light scattering (GPCLALLS), wherein each molecular weight distribution has a peak, and wherein measured detector response of peak I divided by the measured detector response of peak 2 is in the range of from 0.50 to 0.79.
2. The process for polymerizing a polyethylene composition according to claim 1 , wherein the process occurs in a single gas phase reactor, or a dual gas phase reactor.