Ceramic inkjet ink for red decoration
View Patent ↗Disclosed are compositions, such as inkjet inks, for jetting onto a ceramic substrate, and associated methods and systems. The compositions comprise a pigment compound that is configured to be jetted on a ceramic substrate during a ceramic inkjet process to impart a color effect to the ceramic substrate, and a reduction agent which, when exposed to a firing temperature, reacts with the pigment compound to cause a reduction reaction. In some embodiments, the pigment compound comprises jettable copper particles, which can cause the fired composition to take on a red or oxblood color, which can be used for decoration.
1. A composition comprising:
a pigment compound that includes particles of a copper component, wherein the pigment compound is configured to be jetted during an inkjet process, either directly onto a workpiece, or onto a jetted layer on the workpiece, wherein the workpiece is any of a ceramic workpiece or a porcelain workpiece; and
a reduction agent which, when exposed to a firing temperature having a range of 1050 degrees C. to 1300 degrees C., reacts with the pigment compound to form a glaze and cause a reduction reaction that imparts a characteristic red color component to the glaze.
2. The composition of claim 1 , wherein the jetted layer on the workpiece includes one or more jetted colors below the composition.
3. The composition of claim 1 , wherein the jetted layer on the workpiece includes any of a primer or a basecoat.
4. The composition of claim 1 , wherein the workpiece includes a jetted layer over at least a portion of the composition.
5. The composition of claim 4 , wherein the jetted layer over at least a portion of the composition includes one or more jetted clear, translucent or opaque color layers.
6. The composition of claim 1 , wherein the particles of the copper component have a particle size of less than 1 micron.
7. The composition of claim 1 , wherein the copper component includes any of CuO, CuCO 3 , or CuSO 4 .
8. The composition of claim 1 , wherein the reduction agent comprises any of SiO, SiC, SiN, or BN.
9. The composition of claim 1 , wherein the characteristic red color component extends a characteristic color gamut for the composition.
10. The composition of claim 1 , wherein the characteristic red color component has a characteristic wavelength of 620-740 nm upon firing.
11. The composition of claim 1 , wherein the characteristic red color component takes on any of a violet, burgundy, or oxblood color having a characteristic wavelength of 380-440 nm upon firing.
12. The composition of claim 1 , further comprising any of a carrier, a pigment, a dye, or a colorant.
13. A method comprising:
jetting a composition either directly onto a workpiece, or onto a jetted layer on the workpiece, wherein the workpiece comprises any of a ceramic workpiece or a porcelain workpiece, wherein the composition includes:
a pigment compound that includes particles of a copper component, and
a reduction agent; and
causing a color effect to be produced on the workpiece by heating the composition to a firing temperature having a range of 1050 degrees C. to 1300 degrees C., at which the reduction agent reacts with the pigment compound to form a glaze and cause a reduction reaction that imparts a characteristic red color component to the glaze.
14. The method of claim 13 , wherein the jetted layer on the workpiece includes one or more jetted colors below the composition.
15. The method of claim 13 , wherein the jetted layer on the workpiece includes any of a primer or a basecoat.
16. The method of claim 13 , wherein the workpiece includes a jetted layer over at least a portion of the composition.
17. The method of claim 16 , wherein the jetted layer over at least a portion of the composition includes one or more jetted clear, translucent or opaque color layers.
18. The method of claim 13 , wherein the characteristic red color component extends a characteristic color gamut for the composition.
19. The method of claim 13 , wherein the copper component includes any of CuO, CuCO 3 , or CuSO 4 .
20. The method of claim 13 , wherein the particles of the copper component have a particle size of less than 1 micron.
21. The method of claim 13 , wherein the reduction agent comprises any of SiO, SiC, SiN, or BN.
22. The method of claim 13 , wherein the jetting comprises any of:
jetting the pigment compound onto the workpiece, and
jetting the reduction agent onto the jetted pigment compound;
jetting the reduction agent onto the workpiece, and
jetting the pigment compound onto the reduction agent; or
concurrently jetting the pigment compound and the reduction agent onto the workpiece.
23. A printing system comprising:
a print head assembly to jet a composition either directly onto a workpiece, or onto a jetted layer on the workpiece, wherein the workpiece comprises any of a ceramic workpiece or a porcelain workpiece, wherein the composition includes:
a pigment compound that includes particles of a copper component, and
a reduction agent which, when exposed to a firing temperature having a range of 1050 degrees C. to 1300 degrees C., reacts with the pigment compound to form a glaze and cause a reduction reaction that imparts a characteristic red color component to the glaze.
24. A product produced by a process, the process comprising:
jetting a composition either directly onto a workpiece, or onto a jetted layer on the workpiece, wherein the workpiece is any of a ceramic workpiece or a porcelain workpiece, wherein the composition includes:
a pigment compound that includes particles of a copper component, and
a reduction agent; and
causing a color effect to be produced on the workpiece by heating the composition to a firing temperature having a range of 1050 degrees C. to 1300 degrees C., at which the reduction agent reacts with the pigment compound to form a glaze and cause a reduction reaction that imparts a red color component to the glaze;
wherein the product produced by the process includes the workpiece having the color component on the glaze.
25. The product of claim 24 , wherein the jetted layer on the workpiece includes one or more jetted colors below the composition.
26. The product of claim 24 , wherein the jetted layer on the workpiece includes any of a primer or a basecoat.
27. The product of claim 24 , wherein the workpiece includes a jetted layer over at least a portion of the composition.
28. The product of claim 27 , wherein the jetted layer over at least a portion of the composition includes one or more jetted clear, translucent or opaque color layers.