Method of manufacturing OSB with acoustic dampening properties
A manufacturing process for manufacturing wood products with acoustic dampening properties. A noise-dampening polymer is introduced in-line in the manufacturing process to achieve higher acoustic performance. The polymer can be a viscoelastic polymer which is added during blending of the lignocellulosic strands prior to mat formation, or sprayed or otherwise coated on the lignocellulosic strands during mat formation, prior to formation of any boards or panels.
1. A manufactured wood product, comprising:
a panel with a bottom layer, a core layer, and a top layer, with noise-dampening properties formed during a panel manufacturing process with a press configured to apply heat and pressure to a multilayer mat of lignocellulosic material, wherein:
the bottom layer comprises a set of bottom layer lignocellulosic material;
the core layer comprises a set of core layer lignocellulosic material with a noise-reducing polymer mixed with or sprayed upon the core lignocellulosic material prior to insertion of the multilayer mat into the press; and
the top layer comprises a set of top layer lignocellulosic material;
wherein said core layer lignocellulosic material is integrally coated or permeated with the noise-reducing polymer; and
wherein the noise-reducing polymer does not form a homogenous layer.
2. The manufactured wood product of claim 1 , wherein the panel increases airborne sound transmission loss, increases impact sound insulation, and decreases sound pressure levels.
3. The manufactured wood product of claim 2 , wherein the panel increases airborne transmission loss in sound frequency ranges from about 2 K to about 3.2 K Hz.
4. A manufactured wood product, comprising:
a manufactured wood panel with multiple lignocellulosic material-based layers, wherein one or more of said multiple lignocellulosic material-based layers comprise a noise-reducing polymer integrally coating or permeating the lignocellulosic material forming said one or more layers through application of heat and pressure during formation of the manufactured wood panel;
wherein the noise-reducing polymer does not form a homogenous layer.
5. The manufactured wood product of claim 4 , wherein the multiple layers comprise a bottom layer, a core layer, and a top layer.
6. The manufactured wood product of claim 5 , wherein the noise-reducing polymer is integrated with the material forming the core layer.
7. The manufactured wood product of claim 5 , wherein the bottom layer, core layer, and top layer each comprises lignocellulosic material.
8. The manufactured wood product of claim 4 , wherein said one or more layers comprise lignocellulosic strands.
9. The manufactured wood product of claim 8 , wherein said noise-reducing polymer is integrated with the lignocellulosic strands by blending the noise-reducing polymer with the lignocellulosic strands prior to formation of said one or more layers.
10. The manufactured wood product of claim 4 , wherein said noise-reducing polymer is integrated with said one or more layers by spraying the noise-reducing polymer on said one or more layers during formation of a multilayer mat.
11. The manufactured wood product of claim 4 , wherein said panel is an OSB panel.
12. The manufactured wood product of claim 4 , wherein the noise-reducing polymer is a viscoelastic polymer.
13. The manufactured wood product of claim 4 , wherein the panel increases airborne sound transmission loss, increases impact sound insulation, and decreases sound pressure levels.
14. The manufactured wood product of claim 13 , wherein the panel increases airborne transmission loss in sound frequency ranges from about 2 K to about 3.2 K Hz.
15. The manufactured wood product of claim 13 , wherein the manufactured wood panel has an apparent impact insulation class rating in a range from about 26 to about 34, as determined by ASTM Standard E-1007.
16. A manufactured wood product, comprising:
a panel with a bottom layer, a core layer, and a top layer, with noise-dampening properties formed during a panel manufacturing process with a press configured to apply heat and pressure to a multilayer mat of lignocellulosic material, wherein:
the bottom layer comprises a set of bottom layer lignocellulosic material with one or more chemicals or additives added prior to insertion of the multilayer mat into the press;
the core layer comprises a set of core layer lignocellulosic material with one or more chemicals or additives added prior to insertion of the multilayer mat into the press, and with a noise-reducing polymer mixed with or sprayed upon the core lignocellulosic material prior to insertion of the multilayer mat into the press; and
the top layer comprises a set of top layer lignocellulosic material with one or more chemicals or additives added prior to insertion of the multilayer mat into the press;
wherein said core layer lignocellulosic material is integrally coated or permeated with the noise-reducing polymer;
wherein the panel increases airborne sound transmission loss, increases impact sound insulation, and decreases sound pressure levels; and
wherein the panel has an apparent impact insulation class rating in a range from about 26 to about 34, as determined by ASTM Standard E-1007.
17. A method for producing a noise-dampening manufactured wood product, comprising the steps of:
treating a set of bottom layer lignocellulosic strands with one or more chemicals or additives;
treating a set of core layer lignocellulosic strands with one or more chemicals or additives;
treating a set of top layer lignocellulosic strands with one or more chemicals or additives;
adding, in a manufacturing production line, a noise-reducing polymer with the lignocellulosic strands in one or more of said layer sets;
forming a multilayer mat with said treated layer sets; and
applying heat and pressure to the multilayer mat to form one or more panels according to claim 4 .
18. The method of claim 17 , further comprising the step of post-press processing of the one or more boards to produce one or more panels.
19. The method of claim 18 , wherein the one or more panels are OSB panels.
20. The method of claim 17 , wherein the noise-reducing polymer is a viscoelastic polymer.
21. The method of claim 17 , wherein the noise-reducing polymer is added to the set of core layer lignocellulosic strands.
22. The method of claim 17 , wherein the step of adding the noise-reducing polymer comprises blending the noise-reducing polymer with the lignocellulosic strands prior to formation of the multilayer mat.
23. The method of claim 17 , wherein the step of adding the noise-reducing polymer comprises spraying, flowing, curtain or otherwise coating one or more layers of the multilayer mat with the noise-reducing polymer during formation of the multilayer mat.