IP Library Granted Patent US 11,179,780
Granted Patent B2
US 11,179,780 · App. 15/835,520 · Granted Nov 23, 2021

Fabrication of metallic parts by additive manufacturing

View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 11,179,780
App. No.
15/835,520
Granted
Nov 23, 2021
Kind
B2
Abstract

In various embodiments, metallic alloy powders are utilized as feedstock, or to fabricate feedstock, utilized in additive manufacturing processes to form three-dimensional metallic parts. Such three-dimensional parts are fabricated by providing a powder bed containing particles each comprising a mixture and/or alloy of constituent elemental metals, forming a first layer of the part by (i) dispersing a binder into the powder bed, and (ii) curing the binder, the first layer of the shaped part comprising particles bound together by cured binder, disposing a layer of the particles over the first layer of the part, forming subsequent layers of the part, and then sintering the part.

Claims (45)

1. A method of fabricating a three-dimensional object comprising a metallic alloy composed of a plurality of constituent elemental metals, the method comprising:

forming a powder blend by blending together powders of each of the constituent elemental metals;

forming a slurry by mixing the powder blend with a liquid, the liquid comprising water and/or one or more organic binders;

spraying the slurry and a heated gas into a drying chamber to form a plurality of agglomerate particles each comprising a mixture of the plurality of constituent elemental metals;

densifying the agglomerate particles by plasma densification to form composite particles, wherein the agglomerate particles are densified by plasma densification at a temperature less than a melting point of tungsten and greater than melting points of niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, and yttrium;

thereafter, providing a dry powder bed containing the composite particles, wherein the composite particles have a Hall flow rate ranging from approximately 1 s/50 g to approximately 25 s/50 g;

forming a first layer of a shaped part by (i) dispersing a binder into the powder bed, and (ii) curing the binder, the first layer of the shaped part comprising composite particles bound together by cured binder;

disposing a layer of the composite particles over the first layer of the shaped part;

forming subsequent layers of the shaped part by (i) dispersing binder over the composite particles, and (ii) curing the binder, additional composite particles being disposed over the shaped part between layers; and

sintering the shaped part to remove binder therefrom and densify the shaped part, thereby forming the three-dimensional object.

2. The method of claim 1 , wherein each of the composite particles comprises a plurality of grains surrounded by a matrix, the grains comprising one of the elemental metals, and the matrix comprising the others of the elemental metals.

3. The method of claim 2 , wherein the grains comprise tungsten, and the matrix comprises one or more of nickel, iron, or cobalt.

4. The method of claim 1 , wherein the metallic alloy comprises 90% or more of tungsten and 10% or less of one or more additional metals selected from the group consisting of nickel, iron, and cobalt.

5. The method of claim 1 , wherein the shaped part is sintered in a hydrogen-containing atmosphere.

6. The method of claim 1 , wherein the shaped part is sintered at a temperature ranging between approximately 1400° C. and approximately 1500° C.

7. The method of claim 1 , wherein, during formation of each layer of the shaped part, the binder is cured via application of at least one of light or heat.

8. The method of claim 1 , wherein the metallic alloy is composed of a primary element and one or more secondary elements, and a melting point of the primary element is at least 1000° C. higher than a melting point of each said secondary element.

9. The method of claim 1 , wherein the constituent elemental metals are two or more of tungsten, niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, or yttrium.

10. A method of fabricating a three-dimensional object comprising a metallic alloy composed of a plurality of constituent elemental metals, wherein each constituent elemental metal is selected from the list consisting of tungsten, niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, and yttrium, the method comprising:

providing a dry powder bed containing particles (i) each comprising a mixture of the plurality of constituent elemental metals, (ii) having a Hall flow rate ranging from approximately 1 s/50 g to approximately 25 s/50 g, and (iii) formed at least in part by spray drying of a slurry containing a blend of powders of each of the constituent elemental metals, and, thereafter, densification by plasma densification performed at a temperature less than a melting point of tungsten and greater than melting points of niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, and yttrium;

forming a first layer of a shaped part by (i) dispersing a binder into the powder bed, and (ii) curing the binder, the first layer of the shaped part comprising particles bound together by cured binder;

disposing a layer of the particles over the first layer of the shaped part;

forming subsequent layers of the shaped part by (i) dispersing binder over the particles, and (ii) curing the binder, additional particles being disposed over the shaped part between layers; and

sintering the shaped part to remove binder therefrom and densify the shaped part, thereby forming the three-dimensional object.

11. The method of claim 10 , wherein the metallic alloy comprises 90% or more of tungsten and 10% or less of one or more additional metals selected from the group consisting of nickel, iron, and cobalt.

12. The method of claim 10 , wherein the shaped part is sintered in a hydrogen-containing atmosphere.

13. The method of claim 10 , wherein the shaped part is sintered at a temperature ranging between approximately 1400° C. and approximately 1500° C.

14. The method of claim 10 , wherein, during formation of each layer of the shaped part, the binder is cured via application of at least one of light or heat.

15. The method of claim 10 , wherein each of the particles comprises a plurality of grains surrounded by a matrix, the grains comprising one of the constituent elemental metals, and the matrix comprising the others of the constituent elemental metals.

16. The method of claim 15 , wherein the grains comprise tungsten, and the matrix comprises one or more of nickel, iron, or cobalt.

17. The method of claim 10 , wherein the metallic alloy is composed of a primary element and one or more secondary elements, and a melting point of the primary element is at least 1000° C. higher than a melting point of each said secondary element.

18. The method of claim 10 , wherein the constituent elemental metals are two or more of tungsten, niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, or yttrium.

19. A method of fabricating a three-dimensional object comprising a metallic alloy composed of a first constituent elemental metal and one or more second constituent elemental metals, wherein the first constituent elemental metal is selected from the list consisting of tungsten, niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, and yttrium, and each second constituent elemental metal is different from the first constituent elemental metal and selected from the list consisting of tungsten, niobium, tantalum, rhenium, molybdenum, iron, nickel, cobalt, vanadium, palladium, zirconium, and yttrium, the method comprising:

providing a dry powder bed containing particles each comprising a mixture and/or alloy of the first constituent elemental metal and the one or more second constituent elemental metals, wherein the particles have a Hall flow rate ranging from approximately 1 s/50 g to approximately 25 s/50 g;

forming a first layer of a shaped part by (i) dispersing a binder into the powder bed, and (ii) curing the binder, the first layer of the shaped part comprising particles bound together by cured binder;

disposing a layer of the particles over the first layer of the shaped part;

forming subsequent layers of the shaped part by (i) dispersing binder over the particles, and (ii) curing the binder, additional particles being disposed over the shaped part between layers; and

sintering the shaped part to remove binder therefrom and densify the shaped part, thereby forming the three-dimensional object,

wherein the particles are densified, substantially spherical composite particles, each of the composite particles comprising a plurality of grains surrounded by a matrix, the grains comprising the first constituent elemental metal, and the matrix comprising the one or more second constituent elemental metals.

20. The method of claim 19 , wherein the first constituent elemental metal is tungsten, the metallic alloy comprises 90% or more of tungsten, and the metallic alloy comprises 10% or less of the one or more second constituent elemental metals.

21. The method of claim 19 , wherein the shaped part is sintered in a hydrogen-containing atmosphere.

22. The method of claim 19 , wherein the shaped part is sintered at a temperature ranging between approximately 1400° C. and approximately 1500° C.

23. The method of claim 19 , wherein, during formation of each layer of the shaped part, the binder is cured via application of at least one of light or heat.

24. The method of claim 19 , wherein the first constituent elemental metal is tungsten.

25. The method of claim 19 , wherein the three-dimensional object contains pores after sintering, and further comprising infiltrating the pores with a material different from the metallic alloy.

Assignments (5)
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Feb 3, 2026
From: H.C. STARCK SOLUTIONS EUCLID, LLC
To: ELMET TECHNOLOGIES, LLC
Reel/Frame 073679/0340 →
SECURITY INTEREST Recorded Nov 6, 2023
From: H.C. STARCK SOLUTIONS COLDWATER, LLC; H.C. STARCK SOLUTIONS EUCLID, LLC
To: WELLS FARGO BANK, NATIONAL ASSOCIATION
Reel/Frame 065472/0843 →
CHANGE OF NAME Recorded Nov 1, 2023
From: EUCLID FACILITY HOLDINGS, LLC
To: H.C. STARCK SOLUTIONS EUCLID, LLC
Reel/Frame 065415/0762 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Oct 31, 2023
From: H.C. STARCK INC.
To: EUCLID FACILITY HOLDINGS, LLC
Reel/Frame 065402/0594 →
ASSIGNMENT OF ASSIGNOR'S INTEREST Recorded Oct 18, 2021
From: STAWOVY, MICHAEL T.; OHM, SCOTT D.; FILL, FAHRRON C.
To: H.C. STARCK INC.
Reel/Frame 057821/0794 →