Hydrophilic anti-fog coatings

1. A chemically resistant, optically clear transparent anti-fog coating for optically transparent surfaces comprising 1-5% by weight of colloidal silica particles and 0.1 to 10% by volume of porous organo silicate micelles in a polyurethane matrix,

a. the colloidal silica particles having substantially uniform diameters from 10 to 60 nanometers and a residual water content of less than 1.5% w ; and

b. the porous organosilicate micelles being 5-10 nanometers in size, each micelle having a porous hydrophilic silicate shell and a hydrophilic or hydrophobic micellar core.

2. The coating of claim 1 wherein the colloidal silica particles have substantially uniform diameters from 25 to 35 nanometers.

3. The coating of claim 1 wherein the colloidal silica particles have substantially uniform diameters of about 30 nanometers.

4. The coating of claim 1 wherein the porous organosilicate micelles are 7-10 nanometers in diameter.

5. The coating of claim 1 wherein colloidal silica particles comprise 5-8% volume of the porous organosilicate micelles.

6. The coating of claim 1 where the organosilicate micelles are formed from precursors selected from the following group consisting of N-(Acetylglycyl)-3-minopropyltrimethoxy silane, 2-[(Acetoxy(polyethyleneoxy)propyl]triethoxysilane, and 3-cyanopropyltrimethoxysilane.

7. An anti-fog coating for an optically clear plastic or glass substrate, said coating providing protection to the optically clear plastic or glass substrate from organic solvents, wherein the coating for the optically clear plastic substrate comprises monosized, 10-60 nm colloidal silica particles and porous organosilicate micelles in a polyurethane matrix wherein,

the monosized colloidal silica nanoparticles comprising 1-5% by weight of the coating and absorb water droplets or moisture so as to provide a sheeting action at the coating surface; and,

the porous organosilicate micelles having diameters of 5-10 nm comprise 0.1 to 10% v of the coating, said micelles having a hydrophilic core that functions as a moisture reservoir providing hydrophilic properties and fogging resistance to coated substrate.

8. The coating of claim 7 wherein the colloidal silica particles have substantially uniform diameters from 25 to 35 nanometers.

9. The coating of claim 7 wherein the colloidal silica particles have substantially uniform diameters of about 30 nanometers.

10. The coating of claim 7 wherein the porous organosilicate micelles are 7-10 nanometers in diameter.

11. The coating of claim 7 wherein colloidal silica particles comprise 5-8% volume of the porous organosilicate micelles.

12. The coating of claim 7 where the organosilicate micelles are formed from precursors selected from the following group consisting of N-(Acetylglycyl)-3-minopropyltrimethoxy silane, 2-[(Acetoxy(polyethyleneoxy)propyl]triethoxysilane, and 3-cyanopropyltrimethoxysilane.

13. The anti-fog coating of claim 7 wherein the optically clear glass substrate further includes a primer applied thereto before addition of the coating.

14. The anti-fog coating of claim 13 wherein the plastic substrate is selected from the group consisting of polycarbonate, polyurethane, nylon and polyester.

15. A method of forming an anti-fog coating for optically transparent substrates, said coating providing protection to the substrate from organic solvents comprising monosized, 10-60 nm colloidal silica particles and porous organosilicate micelles in a polyurethane matrix comprising

a) dissolving a polyurethane prepolymer in a solvent comprising a mixture of tertiary amyl alcohol and diacetone alcohol to form a prepolymer solution, the solvent mixture comprising 10-40% w of prepolymer solution,

b) disbursing the colloidal silica particles and porous organosilicate micelles in the prepolymer solution, to form a coating solution, the coating solution formulated to have a different viscosities deemed suitable for application to the substrate by dipping, flow application or spray coating,

c) applying the coating solution to the substrate, with or without a primer, and

d) crosslinking the polyurethane prepolymer by exposing the coated substrate to elevated temperatures and/or UV light to form an optically clear cured coating on the substrate.

16. The method of claim 15 wherein the optically clear cured coating is resistant to clouding, swelling, blistering, pitting, peeling, delamination or discoloration by exposure to water or chemical contaminants.

17. The method of claim 15 wherein the colloidal silica particles have substantially uniform diameters from 25 to 35 nanometers.

18. The method of claim 15 wherein the colloidal silica particles have substantially uniform diameters of about 30 nanometers.

19. The method of claim 15 wherein the optically clear cured coating is resistant to clouding, swelling, blistering, pitting, peeling, delamination or discoloration by exposure to water or chemical contaminants.

20. The method of claim 15 wherein the optically clear cured coating is resistant to clouding, swelling, blistering, pitting, peeling, delamination or discoloration by exposure to salt water, gasoline, diesel fuel, jet fuel (JP-8), Ca(OCl) 2 , cleaner/lubricants for weapons, aqueous film-forming foam, aqueous potassium carbonate (K 2 CO 3 , powdered potassium bicarbonate based fire retardant (KHCO 3 ) and 12-15% NaHCO 3 ).