APCHA as a building block in curing agent formulations for structural adhesives
View Patent ↗The invention relates to structural adhesive compositions and more particularly to two-component (2K) structural adhesive compositions. The two components chemically react to bond structural surfaces. N-(3-Aminopropyl)cyclohexylamine (APCHA) has been found to be an improved curing agent for use with epoxy resins in 2K adhesive compositions. APHCA exhibits favorable features including viscosity, pot life and reactivity, and adhesive and thermal performance after curing with epoxy resin. These features and its unique chemistry allow the use of APCHA in curing agent formulations for structural adhesives, in particular wind turbine blade adhesives. APCHA solves issues with viscosity build-up, working time, through-cure, compatibility and adhesive performance that cannot be addressed with the commonly used amine formulations.
1. An adhesive composition comprising the reaction product of:
an epoxy resin component comprising at least one epoxy resin; and
a curing agent component comprising an amine formulation, wherein the amine formulation comprises a first amine component consisting of N-(3-aminopropyl)cyclohexylamine, and a second amine component consisting of at least one selected from the group of polyamides, cycloaliphatic amines, polyether diamines, and ether diamines, wherein the first amine component is 5% to 50% by weight of the amine formulation, and wherein the amine formulation is 10% to 60% by weight of the curing agent component.
2. The adhesive composition of claim 1 , wherein the amine formulation comprises at least one polyamide, wherein the at least one polyamide is 10% to 60% by weight of the amine formulation.
3. The adhesive composition of claim 1 , wherein the amine formulation comprises at least one cycloaliphatic amine, wherein the at least one cycloaliphatic amine is 10% to 40% by weight of the amine formulation.
4. The adhesive composition of claim 1 , wherein the amine formulation comprises at least one polyether diamine, wherein the at least one polyether diamine is 10% to 50% by weight of the amine formulation.
5. The adhesive composition of claim 1 , wherein the amine formulation comprises at least one ether diamine, wherein the at least one ether diamine is up to 30% by weight of the amine formulation.
6. The adhesive composition of claim 1 , wherein the first amine component is 10% by weight of the amine formulation.
7. The adhesive composition of claim 6 , wherein the amine formulation comprises at least one polyamide, wherein the at least one polyamide is 40% by weight of the amine formulation.
8. The adhesive composition of claim 7 , wherein the amine formulation further comprises at least one cycloaliphatic amine, wherein the at least one cycloaliphatic amine is 15% by weight of the amine formulation.
9. The adhesive composition of claim 8 , wherein the amine formulation further comprises at least one polyether diamine, wherein the at least one polyether diamine is 20% by weight of the amine formulation.
10. The adhesive composition of claim 9 , wherein the amine formulation further comprises at least one ether diamine, wherein the at least one ether diamine is 15% by weight of the amine formulation.
11. The adhesive composition of claim 1 , wherein the at least one epoxy resin comprises bisphenol A diglycidyl ether.
12. The adhesive composition of claim 11 , wherein the bisphenol A diglycidyl ether is 40% to 90% by weight of the epoxy resin component.
13. The adhesive composition of claim 1 , wherein the ratio by weight of the epoxy resin component to the curing agent component is from 100/65 to 100/85.
14. The adhesive composition of claim 1 , wherein the curing agent component further comprises at least one selected from the group of talc, fumed silica, aluminum, and amine-terminated butadiene-acrylonitrile copolymers.
15. A wind turbine blade, comprising:
a first portion adhered to a second portion by an adhesive composition disposed between the first portion and the second portion,
wherein the adhesive composition comprises the reaction product of an epoxy resin component comprising at least one epoxy resin, and a curing agent component, wherein the curing agent component comprises a first amine component, the first amine component consisting of N-(3-aminopropyl)cyclohexylamine, and
wherein the wind turbine blade further comprises a blade length, wherein the blade length is greater than 30 meters.
16. A method for forming a wind turbine blade, comprising:
(a) mixing an epoxy resin component comprising at least one epoxy resin with a curing agent component comprising an amine formulation wherein the amine formulation comprises a first amine component consisting of N-(3-aminopropyl)cyclohexylamine to form an adhesive composition;
(b) applying the adhesive composition to a first portion of a wind turbine blade and a second portion of the wind turbine blade;
(c) after step (b), coupling the first portion of the wind turbine blade to a second portion of the wind turbine blade by contacting the second portion to the adhesive composition applied to the first portion of the wind turbine blade;
(d) pressing the first portion and the second portion of the wind turbine blade together for a sufficient period of time to allow the adhesive composition to cure.
17. The method of claim 16 , further comprising, after step (c), heating the first portion and the second portion of the wind turbine blade to aid in the curing process.