Granted Patent B2

US 11,292,280 · App. 15/855,608 · Granted Apr 5, 2022

Abstract

Claims (27)

1. A silicone release coating material for a thermally-responsive record material useful for linerless labels,

comprising, before being cured, an aqueous mixture of a release coating layer material and a hydrophilic silica,

wherein the release coating layer material weighs 28.7%-40.0% of the silicone release coating material,

wherein the release coating layer material comprises a silicone emulsion, a silicone crosslinker emulsion and a platinum catalyst, wherein the silicone emulsion weighs 70.8% of the release coating layer material, the silicone crosslinker emulsion weighs 16.2% of the release coating layer material, and the platinum catalyst weighs 13.0% of the release coating layer material,

wherein the hydrophilic silica is precipitated silica or fumed silica, the hydrophilic silica weighs 20%-30% of dry components of the silicone release coating material,

wherein the silicone release coating material is configured to be deposited on the thermally-responsive record material comprising a substrate having first and second surfaces, at least the first surface comprising:

a binder; and

a heat sensitive coating having one or more layers of a colorless dye precursor and an acidic developer material in contiguous relationship,

wherein the silicone release coating material is formed in direct contact with the heat sensitive coating,

wherein the heat sensitive coating upon being heated reacts with the colorless dye precursor to develop color, and

wherein the silicone release coating material is cured at a temperature at or below 160° C.

2. The silicone release coating material according to claim 1 , wherein an excess of platinum catalyst is greater than 191 ppm, based on the total weight of the silicone release coating material.

3. The silicone release coating material according to claim 1 , wherein the fumed silica has a surface area over 175 m 2 /g.

4. The silicone release coating material according to claim 1 , wherein the thermally-responsive record material includes in addition an adhesive layer on the second surface of the substrate.

5. The silicone release coating material according to claim 1 , wherein the platinum catalyst is selected from a group consisting of a metallic platinum, a platinum salt, and an organic platinum compound.

6. The silicone release coating material according to claim 1 , wherein the platinum catalyst has an oxidation state from 0 to IV.

7. The silicone release coating material according to claim 1 , wherein the platinum catalyst comprises a platinum catalyst selected from the group consisting of chloroplatinic acid and olefin complexes, platinum (0) complexes containing vinyl-siloxane ligands, platinum (II) chloride, salts of chloroplatinic acid, tetrachloroplatinic acid, platinum (IV) chloride, hexachloroplatinic acid, hexachloroplatinic acid ammonium salt, platinum (II) oxide, platinum (II) hydroxide, platinum (IV) dioxide, platinum (IV) oxide, platinum (IV) disulfide, platinum (IV) sulfide, potassium hexachloroplatinate (IV), dichloro(cycloocta-1,5-diene) platinum (II), and ammonium salts of chloroplatinic acid.

8. The silicone release coating material according to claim 1 , wherein the silicone release coating material is applied at a rate of 1 to 6 grams per square meter (gsm).

9. A method of providing a thermally-responsive record material useful for linerless labels with a silicone release coating material, the thermally-responsive record material comprising a support having first and second surfaces, the method comprising:

applying to at least the first surface of the support a heat sensitive color-forming composition comprising a binder material and a colorless dye precursor and an acidic developer material in contiguous relationship;

applying the silicone release coating material over the heat sensitive color-forming composition, the silicone release coating material comprising an aqueous mixture of a release coating layer material and a hydrophobic silica, wherein the release coating layer material weighs 28.7%-40.0% of the silicone release coating material, wherein the release coating layer material comprises a silicone emulsion, a silicone crosslinker emulsion and a platinum catalyst, wherein the silicone emulsion weighs 70.8% of the release coating layer material, the silicone crosslinker emulsion weighs 16.2% of the release coating layer material, and the platinum catalyst weighs 13.0% of the release coating layer material, wherein the hydrophilic silica is precipitated silica or fumed silica, the hydrophilic silica is weighs 20%-30% of dry components of the silicone release coating material, wherein the silicone release coating material is in direct contact with the heat sensitive color-forming composition; and

curing the silicone release coating material at a temperature at or below 160° C.

10. The method according to claim 9 , wherein an excess of platinum catalyst is greater than 191 ppm, based on the total weight of the silicone release coating material.

11. The method according to claim 9 , wherein the fumed silica has a surface area over 175 m 2 /g.

12. The method according to claim 9 , wherein the platinum catalyst has an oxidation state from 0 to IV.

13. The method according to claim 9 , wherein the platinum catalyst comprises a platinum catalyst selected from the group consisting of chloroplatinic acid and olefin complexes, platinum (0) complexes containing vinyl-siloxane ligands, platinum (II) chloride, salts of chloroplatinic acid, tetrachloroplatinic acid, platinum (IV) chloride, hexachloroplatinic acid, hexachloroplatinic acid ammonium salt, platinum (II) oxide, platinum (II) hydroxide, platinum (IV) dioxide, platinum (IV) oxide, platinum (IV) disulfide, platinum (IV) sulfide, potassium hexachloroplatinate (IV), dichloro(cycloocta-1,5-diene) platinum (II), and ammonium salts of chloroplatinic acid.

14. The method according to claim 9 , wherein the silicone release coating material is applied at a rate of 1 to 6 grams per square meter (gsm).