Carbon fiber zinc negative electrode
View Patent ↗The conductivity of a zinc negative electrode is enhanced through use of surfactant-coated carbon fibers. Carbon fibers, along with other active materials such as bismuth oxide, zinc etc., form an electronically conductive matrix in zinc negative electrodes. Zinc negative electrodes as described herein are particularly useful in nickel zinc secondary batteries.
1. A method of fabricating a zinc negative electrode, the method comprising:
(i) coating a material selected from the group consisting of lead, tin, and combinations thereof onto zinc particles comprising at least one material selected from the group consisting of zinc and zinc oxide to form coated zinc particles;
(ii) coating carbon particles with a surfactant to make coated carbon particles;
(iii) forming a paste from the coated zinc particles, coated carbon particles, bismuth oxide, a dispersing agent, a binding agent, and a liquid; and
(iv) incorporating the paste into the zinc negative electrode.
2. The method of claim 1 , wherein the carbon particles are carbon fibers.
3. The method of claim 2 , wherein the carbon fibers are metallized.
4. The method of claim 3 , wherein the carbon fibers are metallized with a material comprising a metal selected from the group consisting of lead, tin, indium, bismuth and silver.
5. The method of claim 1 , wherein the coated zinc particles are less than 40 microns in size.
6. The method of claim 4 , wherein the zinc particles are coated with lead and the lead comprises less than about 0.05% by weight of a negative electrode active material.
7. The method of claim 2 , wherein the zinc negative electrode comprises less than 3% by weight of the carbon fiber by dry weight of the zinc negative electrode.
8. The method of claim 2 , wherein the carbon fiber is between about 10 μm and 500 μm in length, and between about 1 μm and 50 μm in diameter, with a ratio of length to width of between about 50:1 and about 10:1.
9. The method of claim 2 , wherein the surfactant comprises at least one of a polyglycol non-ionic surfactant, a poloxamer and a fluorosurfactant.
10. The method of claim 2 , wherein the liquid comprises a liquid selected from the group consisting of water, an alcohol and an ether.
11. A method of fabricating a zinc negative electrode, comprising:
(i) treating carbon particles with a surfactant to produce surfactant-coated carbon particles;
(ii) combining the surfactant-coated carbon particles with, at least, electrochemically active zinc to produce an evenly dispersed mixture; and
(iii) coating a substrate current collector with the evenly dispersed mixture.
12. The method of claim 11 , wherein the carbon particles are carbon fibers.
13. The method of claim 12 , further comprising heating the substrate current collector after (iii).
14. The method of claim 13 , wherein the substrate current collector is heated under inert atmosphere to between about 250° C. and about 300° C. for between about 30 minutes and about 60 minutes.
15. The method of claim 11 , wherein the surfactant comprises at least one of a polyglycol non-ionic surfactant, a poloxamer and a fluorosurfactant.