Substrate coated with non-stick coating resistant to abrasion and scratching
A substrate coated with a non-stick fluoropolymer coating is provided, the coating having excellent abrasion and scratch resistance. The coating contains: i.) a continuous primer layer adhered to the substrate containing a polymer binder, a first fluoropolymer and first inorganic film hardner particles, ii.) a discontinuous midcoat layer containing aggregate particles adhered to the primer layer and distributed discontinuously across the surface of the primer layer so as to reveal exposed areas of the surface of the primer layer, wherein a portion of the aggregate particles are in clusters, and wherein the aggregate particles contain second fluoropolymer and second inorganic film hardner particles, and iii.) a topcoat layer containing a third fluoropolymer adhered to the midcoat layer and the exposed areas of the surface of the primer layer at points where there is no midcoat layer.
1. A substrate coated with a non-stick coating resistant to abrasion and scratching, said non-stick coating comprising:
i.) a continuous primer layer adhered to said substrate, said continuous primer layer comprising a polymer binder, a first fluoropolymer and first inorganic film hardener particles,
ii.) a discontinuous midcoat layer comprising aggregate particles adhered to said continuous primer layer and distributed discontinuously across the surface of said continuous primer layer so as to reveal exposed areas of the surface of said continuous primer layer, wherein from about 5 percent to about 20 percent of said aggregate particles are in clusters having a diameter of at least about 0.1 mm and height of at least 0.02 mm as measured from the surface of said continuous primer layer, and wherein said aggregate particles comprise a second fluoropolymer and second inorganic film hardener particles, and
iii.) a topcoat layer comprising a third fluoropolymer adhered to said discontinuous midcoat layer and said exposed areas of the surface of said continuous primer layer
wherein said first inorganic film hardener particles and said second inorganic film hardener particles independently comprise ceramic particles having a Knoop hardness of at least about 1,200.
2. The substrate of claim 1 , wherein said first fluoropolymer is PTFE, said second fluoropolymer is PTFE that is the same or different from said PTFE of said first fluoropolymer, and said third fluoropolymer is PFA or MFA.
3. The substrate of claim 1 , wherein said fluoropolymers as a component of each layer of said coating comprises about 10 to about 45 weight percent of all cured components of said continuous primer layer, at least about 70 weight percent of all cured components of said discontinuous midcoat layer, and at least about 90 weight percent of all cured components of said topcoat layer.
4. The substrate of claim 1 , wherein the average particle size of the first inorganic film hardener particles in said continuous primer layer ranges from about 10 to about 60 microns, and the average particle size of the second inorganic film hardener particles in said discontinuous midcoat layer ranges from about 5 to about 44 microns.
5. The substrate of claim 1 , wherein said aggregate particles comprising said second fluoropolymer and said second inorganic film hardener particles have an average particle size of from about 0.1 to about 4 mm.
6. The substrate of claim 1 , wherein said aggregate particles comprising said second fluoropolymer and said second inorganic film hardener particles have an average particle size of from about 0.1 to about 1 mm.
7. The substrate of claim 1 , wherein said clusters have a diameter at least about 0.2 mm.
8. The substrate of claim 1 , wherein said clusters have a diameter of at least about 0.2 mm to about 4 mm.
9. The substrate of claim 1 , wherein said clusters have a height in the range of from 0.02 mm to no greater than about 0.1 mm.
10. The substrate of claim 1 , wherein said clusters have a height in the range of from 0.02 mm to no greater than about 0.07 mm.
11. The substrate of claim 1 , wherein about 15 percent of the number of aggregate particles are contained in clusters.
12. The substrate of claim 1 , wherein said discontinuous midcoat layer has a weight per square meter on a cured basis of from about 0.05 g/m 2 to about 0.25 g/m 2 .
13. The substrate of claim 1 , wherein said discontinuous midcoat layer has a weight per square meter on a cured basis of from about 0.1 g/m 2 to about 0.2 g/m 2 .
14. The substrate of claim 1 , wherein said discontinuous midcoat layer has a weight per square meter on a cured basis of from about 0.12 g/m 2 to about 0.18 g/m 2 .
15. The substrate of claim 1 , wherein said first inorganic film hardener particles and said second inorganic film hardener particles are independently selected from the group consisting of inorganic oxides, nitrides, borides and carbides of zirconium, tantalum, titanium, tungsten, boron, aluminum and beryllium.
16. The substrate of claim 1 , wherein said first inorganic film hardener particles and said second inorganic film hardener particles comprise silicon carbide.
17. The substrate of claim 1 , wherein said first inorganic film hardener particles and said second inorganic film hardener particles comprise aluminum oxide.
18. The substrate of claim 1 , wherein the non-stick coating has a Computer Aided Mechanical Utensil Tester (CAMUT) test rating of 9.