Composition and method for producing a textured acrylic surface
A composition for making a cast, thermoformable sheet or slab, comprising: a syrup comprising: about 30-40% SSI—acrylic pre-polymerized syrup by weight at 20% solids; about 30-40% MMA—methyl methacrylate by weight; about 2-3% BA—Butyl acrylate by weight; about 1-15% by weight acrylic chips; and about 1-15% by weight rigid particles with a mean diameter of about 0.5-2000 μm. The rigid particles may preferably comprise a polymeric material such as poly allyl diglycol carbonate particles. A method for producing a thermoformed article having a textured surface comprising mixing the syrup as above; swelling the acrylic chips; degassing the syrup; heating the syrup; casting the syrup into a sheet; and thermoforming the cast sheet against a mold.
1. A composition for making a cast, thermoformable sheet or slab, providing a nonslip surface, comprising: a syrup comprising:
a) about 30-40% Acrylic pre-polymerized syrup by weight at 20% solids;
b) about 30-40% MMA—methyl methacrylate by weight;
c) about 2-3% BA—Butyl acrylate by weight;
d) about 1-15% acrylic chips by weight; and
e) about 1-15% rigid particles, by weight,
wherein the rigid particles comprise poly allyl diglycol carbonate, with a mean diameter of about 0.5-2000 μm.
2. The composition of claim 1 wherein the syrup comprises:
a. about 38% Acrylic pre-polymerized syrup at 20% solids by weight;
b. about 38% MMA—methyl methacrylate by weight;
c. about 3% BA—Butyl acrylate by weight;
d. about 14% acrylic chips by weight; and
e. about 7% rigid particles, by weight with a mean diameter of about 0.5-2000 μm.
3. The composition of claim 1 wherein the syrup further comprises one or more of an anti-flocculating agent; a pigment; a chain transfer agent; a release agent; a crosslinking agent and an initiator.
4. The composition of claim 1 wherein the syrup further comprises one or more of an anti-flocculating agent; a pigment; a chain transfer agent; a release agent; a crosslinking agent and an initiator.
5. A composition for making a cast, thermoformable sheet or slab, providing a nonslip surface, comprising: a syrup, comprising:
a) about 37.7% Acrylic pre-polymerized syrup by weight at 20% solids;
b) about 37.7% MMA—methyl methacrylate by weight;
c) about 2.7% BA—Butyl acrylate by weight;
d) about 0.3%, by weight, of an anti flocculating agent;
e) about 0.1%, by weight, of a chain transfer agent;
f) about 0.01%, by weight, of a release agent;
g) about 0.2%, by weight, of a crosslinking agent;
h) about 0.1-0.3%, by weight, of one or more initiators;
i) about 14% acrylic chips, by weight; and
j) about 7% rigid particles, by weight,
wherein the rigid particles comprise poly allyl diglycol carbonate, with a mean diameter of about 0.5-2000 μm.
6. A method for producing a thermoformed article having a textured surface by mixing a syrup comprising:
a) about 30-40% Acrylic pre-polymerized syrup by weight at 20% solids;
about 30-40% MMA—methyl methacrylate by weight;
about 2-3% BA—Butyl acrylate by weight;
about 1-15% acrylic chips by weight; and
about 1-15% rigid particles, by weight,
wherein the rigid particles comprise poly allyl diglycol carbonate, with a mean diameter of about 0.5-2000 μm;
b) swelling the acrylic chips;
c) degassing the syrup;
d) heating the syrup;
e) casting the syrup into a sheet; and
f) thermoforming the cast sheet against a mold.
7. The method of claim 6 wherein the syrup is cast against a polished surface to produce a sheet having a gloss finish.
8. The method of claim 7 wherein the sheet having a gloss finish is thermoformed against the mold to produce the article.
9. The method of claim 8 wherein the article has one or more textured surfaces and one or more glossy surfaces.
10. The method of claim 6 wherein the rigid particles comprise poly allyl diglycol carbonate.
11. The method of claim 6 wherein the rigid particles comprise poly allyl diglycol carbonate and about 7% of the syrup.
12. The method of claim 6 wherein the syrup comprises:
a) about 37.7% Acrylic pre-polymerized syrup at 20% solids;
b) about 37.7% MMA—methyl methacrylate;
c) about 2.7% BA—Butyl acrylate;
d) about 0.3% of an anti flocculating agent;
e) about 0.1% of a chain transfer agent;
f) about 0.01% of a release agent;
g) about 0.2% of a crosslinking agent;
h) about 0.1-0.3% of one or more initiators;
i) about 14% acrylic chips; and
j) about 7% poly allyl diglycol carbonate particles with a mean diameter of about 0.5-2000 μm.
13. A method for producing a thermoformed article having a textured surface by the steps of:
a) providing the syrup of claim 1 ;
b) swelling the acrylic chips;
c) degassing the syrup;
d) heating the syrup;
e) casting the syrup into a sheet; and
f) thermoforming the cast sheet against a mold.
14. The method of claim 13 wherein the syrup is cast against a polished surface to produce a sheet having a gloss finish.
15. The method of claim 14 wherein the sheet having a gloss finish is thermoformed against the mold to produce the article.
16. The method of claim 15 wherein the article has one or more textured surfaces and one or more glossy surfaces.
17. The method of claim 13 wherein the rigid particles comprise poly allyl diglycol carbonate.
18. The method of claim 13 wherein the rigid particles comprise poly allyl diglycol carbonate and about 7% of the syrup.
19. The method of claim 13 wherein the syrup comprises:
a) about 37.7% Acrylic pre-polymerized syrup at 20% solids;
b) about 37.7% MMA—methyl methacrylate;
c) about 2.7% BA—Butyl acrylate;
d) about 0.3% of an anti flocculating agent;
e) about 0.1% of a chain transfer agent;
f) about 0.01% of a release agent;
g) about 0.2% of a crosslinking agent;
h) about 0.1-0.3% of one or more initiators;
i) about 14% acrylic chips; and
j) about 7% poly allyl diglycol carbonate particles with a mean diameter of about 0.5-2000 μm.