3XX aluminum casting alloys, and methods for making the same
New 3xx aluminum casting alloys are disclosed. The aluminum casting alloys generally include from 6.5 to 11.0 wt. % Si, from 0.20 to 0.80 wt. % Mg, from 0.05 to 0.50 wt. % Cu, from 0.10 to 0.80 wt. % Mn, from 0.005 to 0.05 wt. % Sr, up to 0.25 wt. % Ti, up to 0.30 wt. % Fe, and up to 0.20 wt. % Zn, the balance being aluminum and impurities.
1. A 3xx aluminum alloy shape cast product, consisting of:
6.5-8.9 wt. % Si;
0.55-0.80 wt. % Mg;
0.15-0.35 wt. % Cu;
0.30-0.80 wt. % Mn;
0.012-0.040 wt. % Sr;
up to 0.25 wt. % Ti;
up to 0.12 wt. % Fe; and
up to 0.20 wt. % Zn;
the balance being aluminum (Al) and impurities, wherein the 3xx aluminum alloy shape cast product includes not greater than 0.10 wt. % of any one impurity, and wherein the 3xx aluminum alloy shape cast product includes not greater than 0.35 wt. %, in total, of the impurities;
wherein the 3xx aluminum alloy shape cast ptoduct realizes a quality index of at least 400;
wherein the 3xx aluminum alloy shape cast product is absent of die soldering defects; and
wherein the 3xx aluminum alloy shape cast product includes a suffocoent amount of the Si, Mg, Cu, Mn, Sr, Ti, Fe, Zn, Al, and impurities to achieve a tensile yield strenght of at least 290 MPa and when tested in accordance with ASTM E8 and B557.
2. The 3xx aluminum alloy shape cast product of claim 1 , having at least 7.25 wt. % Si.
3. The 3xx aluminum alloy shape cast product of claim 1 , having at least 8.0 wt. % Si.
4. The 3xx aluminum alloy shape cast product of claim 1 , having not greater than 0.75 wt. % Mg.
5. The 3xx aluminum alloy cast product of claim 1 , having not greater than 0.70 wt. % Mg.
6. The 3xx aluminum alloy shape cast product of claim 1 , having at least 0.18 wt. % Cu.
7. The 3xx aluminum alloy shape cast product of claim 1 , having at least 0.35 wt. % Mn.
8. The 3xx aluminum alloy shape cast product of claim 1 , having not greater than 0.65 wt. % Mn.
9. The 3xx aluminum alloy shape cast product of claim 1 , having from 0.005 to 0.25 wt. % Ti.
10. The 3xx aluminum alloy shape cast product of claim 1 , having not greater than 0.11 wt. % Fe and not greater than 0.15 wt. % Zn.
11. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product includes a sufficient amount of the Si, Mg, Cu, Mn, Sr, Ti, Fe, Zn, Al, and impurities to achieve an elongation of at least 5% when tested in accordance with ASTM E8 and B557.
12. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product includes a sufficient amount of the Si, Mg, Cu, Mn, Sr, Ti, Fe, Zn, Al, and impurities to achieve a quality index of at least 430.
13. The 3xx aluminum alloy shape cast product of claim 1 , having at least 0.60 wt. % Mg.
14. The 3xx aluminum alloy shape cast product of claim 1 , having at least 0.40 wt. % Mn.
15. The 3xx aluminum alloy shape cast product of claim 1 , having at least 0.45 wt. % Mn.
16. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product includes a sufficient amount of the Si, Mg, Cu, Mn, Sr, Ti, Fe, Zn, Al, and impurities to achieve an elongation of at least 6% when tested in accordance with ASTM E8 and B557.
17. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product is an automotive component.
18. The 3xx aluminum alloy shape cast product of claim 17 , wherein the shape cast product is a shape cast body-in-white part or a shape cast suspension part.
19. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product has a wall thickness of from 2 to 5 mm.
20. The 3xx aluminum alloy shape cast product of claim 1 , wherein the 3xx aluminum alloy shape cast product comprises a sufficient amount of alloying elements of Si, Mg, Cu, Mn, Sr, Ti, Fe, Zn, Al, and impurities to achieve an intergranular corrosion resistance that is comparable to the intergranular corrosion resistance of a baseline shaped cast part, wherein the baseline shaped cast part is made from conventional alloy A365, and wherein the intergranular corrosion resistance is tested in accordance with ASTM G110-92 (2015), measured on the as-cast shape cast part (not machined) after 24 hours of exposure.