Malleable demineralized bone composition and method of manufacture
View Patent ↗A malleable demineralized bone composition consists of cortical bone made from a first portion and a second portion. The first portion of cortical bone is made from cut pieces freeze dried then ground into particles and demineralized then freeze-dried. The second portion of cortical bone is shaved into shavings. The shavings are long thin strips subjected to freeze-drying. The freeze-dried shavings are ground and demineralized and then freeze-dried. A volume of the second portion is placed in a solution of sterile water to create a mixture, the water volume being twice the second portion, the mixture is autoclaved under heat and pressure to form a gelatin, and the first portion is mixed with the gelatin to form a malleable putty or paste.
1. A method of making a malleable demineralized bone composition consisting of demineralized bone matrix (DBM) particles of cortical bone and water comprises the steps of:
preparing a first portion of cortical bone by cutting the cortical bone into pieces, freeze-drying the pieces and then grinding into particles and demineralizing the ground particles and thereafter freeze-drying the demineralized ground particles to form a first portion of DBM particles;
preparing a second portion of cortical bone by shaving wherein cortical bone is cut into long pieces, cleaned and then shaved to form shavings of cortical bone tissue then freeze-drying the shavings, grinding the freeze-dried shavings to obtain a particle size less than 150 μm and demineralizing the particles thereafter freeze-drying to form a second portion of DBM particles;
autoclaving a volume of the second portion of DBM particles mixed with sterile water in a 2:1 ratio by volume for a predetermined time of 1.25 hours including condition of 15 minutes, exposure of 30 minutes and drying of 30 minutes at a pre-set temperature and pressure during exposure of 121.1 degrees C. and 30.15 psi respectively to form a gelatin;
cooling the gelatin made from the second portion; and
mixing the freeze-dried ground particles of the first portion with the gelatin from the second portion at a ratio of 80:20 or less gelatin to DBM to create a malleable putty or paste.
2. The method of making a malleable demineralized bone composition of claim 1 wherein the second portion is long strips cut from cortical bone, the strips having a length of greater than 5 cm.
3. The method of making a malleable demineralized bone composition of claim 2 wherein the cortical shavings are ground to a particle size up to 125 microns.
4. The method of making a malleable demineralized bone composition of claim 1 wherein the first portion has the cut pieces having a width, a length and a thickness in the range of 1 to 4 mm.
5. The method of making a malleable demineralized bone composition of claim 1 wherein the cortical bone ground particles of the first portion are less than 1000 microns.
6. The method of making a malleable demineralized bone composition of claim 5 wherein the ground particles of the first portion greater than 100 microns.
7. The method of making a malleable demineralized bone composition of claim 5 wherein the ground particles of the first portion are sieved to a first size range of 125 to 300 microns, a second size range 300 to 500 microns and a third range 500 to 850 microns.
8. The method of making a malleable demineralized bone composition of claim 7 wherein the size first through third ranges have a ratio of 40:40:20 by weight, respectively.
9. The method of making a malleable demineralized bone composition of claim 1 wherein the ratio of gelatin to particles from the first portion is 80:20 by volume.
10. The method of making a malleable demineralized bone composition of claim 1 wherein the mixture formed as a malleable putty or paste is packaged in a capped syringe.
11. The method of making a malleable demineralized bone composition of claim 10 wherein the packaged mixture is stored at room temperature.