Decorative nonwoven laminates
A decorative, nonwoven laminate and a method of forming, including a first side of a first nonwoven affixed to one or both of a) a first side of a polymeric sheet or b) a second nonwoven, wherein the first nonwoven exhibits a basis weight of 15 g/m 2 to 500 g/m 2 and the second nonwoven exhibits a basis weight of 15 g/m 2 to 1200 g/m 2 ; and a colorant deposited on a second side of the first nonwoven. A topical coating may or may not be applied to improve durability of the printed surface layer.
1. A decorative, nonwoven vehicle interior laminate, comprising:
a first side of a first nonwoven affixed to a first side of a single polymeric sheet;
wherein said first nonwoven has a thickness in the range of 0.1 mm to 1.8 mm and a basis weight of 50 g/m 2 to 200 g/m 2 and said polymeric sheet has a thickness in the range of 0.3 mm to 2.0 mm and a basis weight at an areal density in the range of 150 g/m 2 to 1200 g/m 2 ;
a colorant selected from an ink, paint or pigment dye deposited on the surface of a second side of said first nonwoven at a thickness of 0.01 mm to 0.3 mm;
a topical coating applied on said colorant and said second side of said first nonwoven at a thickness of 1.1 mm to 3.0 mm;
a second nonwoven affixed to a second side of said polymeric sheet, wherein said second nonwoven has a thickness of 2.0 mm to 12.0 mm and a basis weight of 300 g/m 2 to 1200 g/m 2 ; characterized by the feature that said first nonwoven, said polymer sheet and said second nonwoven are attached together and said decorative nonwoven laminate has a three-dimensional geometry including projections or depressions;
wherein said laminate with said colorant has a minimum fade resistance ranking of 4 in a xenon test system at 225 kJ/m 2 to 451 kJ/m 2 as measured by ISO 105-A02/AATCC evaluation Procedure 1 and a Taber abrasion of 15,000 cycles using an H18 wheel and 1000 gm weight according to ASTM D3884 or SAE J1530 and said laminate with said three-dimensional geometry is a vehicle interior component.
2. The decorative, nonwoven laminate of claim 1 , wherein said polymeric sheet is one or more polymeric materials selected from the following: polyethylene, polypropylene, polyester, polyamide, co-polyester, ethyl vinyl acetate, thermoplastic elastomer, thermoplastic olefin, and combinations thereof.
3. The decorative laminate of claim 1 wherein said colorant is deposited at discrete locations on the surface of said second side of said first nonwoven.
4. The decorative laminate of claim 1 wherein said first nonwoven has a thickness of 0.4 mm to 1.5 mm.
5. The decorative laminate of claim 1 wherein said topical coating applied on said colorant comprises a thermoplastic elastomer, thermoplastic olefin, polyurethane, high density polyethylene, polypropylene, or glycol modified polyethylene terephthalate.
6. The decorative laminate of claim 1 wherein said topical coating comprises polyurethane at a basis weight of 15 gsm to 340 gsm.