Demineralized bone fiber composition for use in minimally invasive surgery
A bone implant composition and methods thereof include bone material made into various implant shapes including a cylinder having an outermost layer and an inner layer completely surrounded by the outermost layer. The bone implant compositions and methods include a bag or cylindrical tube made from a bone material which may be filled with additional bone material.
1. A method of making a bone implant from a sheet of demineralized bone fibers (DBF) comprising a plurality of elongated bone fibers cut from demineralized bone in a direction parallel to the orientation of collagen fibers, the method comprising:
providing the DBF into a sheet mold to form a sheet of DBF; and
processing the sheet of DBF by:
i) rolling the sheet of DBF to form a cylindrical bone implant or a hollow tube bone implant; or
ii) bonding a first sheet of DBF with a second sheet DBF to form a bone implant bag,
wherein the hollow tube bone implant or the cylindrical bone implant has a length of from about 1 cm to about 30 cm and a diameter of from about 3 mm to about 15 mm.
2. The method of claim 1 , further comprising adding a second bone material to the sheet of DBF prior to rolling the sheet of DBF, the second bone material selected from synthetic bone graft substitute, allograft bone chips, xenograft bone chips, and/or demineralized bone matrix (DBM).
3. The method of claim 1 , wherein rolling the sheet of DBF to form a cylindrical bone implant comprises using a cigarette roller technique.
4. The method of claim 1 , wherein rolling the sheet of DBF to form a hollow tube bone implant comprises hand rolling the sheet around a mandrel.
5. The method claim 4 , wherein the mandrel has an oval cross section.
6. The method of claim 4 , further comprising heating the cylindrical bone implant or the hollow tube bone implant at between 30° to 70° Celsius for 1 minute up to 180 minutes.
7. The method of claim 6 , further comprising filling the hollow tube bone implant with synthetic bone graft substitute, allograft bone chips, xenograft bone chips, and/or demineralized bone matrix (DBM), wherein the filling occurs after heating.
8. The method of claim 1 , wherein the bonding of the first sheet of DBF with the second sheet of DBF to form a bone implant bag comprises annealing together three of four sides of the first sheet and the second sheet forming a cavity therebetween.
9. The method of claim 1 , wherein the bone implant bag has a length from about 5 cm to about 11 cm and a width from about 5 cm to about 11 cm.
10. A method of making a bone implant bag from a sheet of demineralized bone fibers (DBF) comprising:
providing the DBF into a sheet mold to form a sheet of DBF; and
bonding a first sheet of DBF with a second sheet DBF to form a bone implant bag.