Pressed and self sintered polymer derived SiC materials, applications and devices
Organosilicon chemistry, polymer derived ceramic materials, and methods. Such materials and methods for making polysilocarb (SiOC) and Silicon Carbide (SiC) materials having 3-nines, 4-nines, 6-nines and greater purity. Processes and articles utilizing such high purity SiOC and SiC.
1. A silicon carbide composition comprising:
a. polymer derived silicon carbide particles;
b. the particles having a mean particle size of about 0.5 μm or smaller;
c. the particles consisting essentially of silicon and carbon in an SiC 4 configuration, wherein the particles have less than 0.5% excess carbon, and are at least 99.99999% pure.
2. The composition of claim 1 , wherein the mean particle size is about 0.2 μm or smaller.
3. The composition of claim 1 , wherein the mean particle size is about 0.1 μm or smaller.
4. A self sinterable silicon carbide composition comprising:
a. polymer derived silicon carbide particles;
b. the particles having a mean particle size of about 0.5 μm or smaller;
c. the particles consisting essentially of silicon and carbon in an SiC 4 configuration, wherein the particles have less than 0.1% excess carbon, and are at least 99.99999% pure;
d. wherein the particles are capable of being formed into a solid SiC volumetric shape without the need for a sintering aid.
5. The composition of claim 4 , wherein the volumetric shape is a layer.
6. The composition of claim 4 , wherein the volumetric shape, is selected from the group of shapes consisting of a window, a lens, and a fiber.
7. The composition of claim 4 , wherein the volumetric shape is an article selected from the group consisting of armor, ballistic materials, blast shields, penetration resistant materials, windows, lenses, fibers, internal reflection optics, and optics.
8. A silicon carbide composition comprising:
a. polymer derived silicon carbide particles;
b. the particles having a particle size smaller than about 5 μm, each particle having a surface, wherein the surfaces are free from an oxide layer; and,
c. the particles consisting essentially of SiC, wherein the particles are at least 99.99999% pure.
9. The composition of claim 8 , wherein the particle size is smaller than about 1 μm.
10. The composition of claim 8 , wherein the particle size is smaller than about 0.5 μm.
11. The composition of claim 8 , wherein the particle size is smaller than about 0.1 μm.
12. The composition of claim 8 , wherein the particle size is smaller than about 0.05 μm.
13. The composition of claim 8 , comprising a refractory ceramic powder, whereby the composition is a blend.
14. The composition of claim 13 , wherein the refractory ceramic powder comprises a material selected from the group consisting of AlN, BC, BN, Al 2 O 3 , ZrO 2 , and Si.