Anodized quality 5XXX aluminum alloys with high strength and high formability and methods of making the same
Provided herein are anodized quality AA5xxx series aluminum alloys and methods for making the aluminum alloys. Also described herein are products prepared from the anodized quality AA5xxx series aluminum alloy sheets. Such products include consumer electronic parts, consumer electronic product parts, architectural sheet products, architectural sheet product parts, and automobile body parts.
1. An aluminum alloy, comprising 0 to 0.1 wt. % Si, 0 to 0.19 wt. % Fe, 0.01 to 0.3 wt. % Cu, 0.35 to 0.5 wt. % Mn, 2.0 to 3.5 wt. % Mg, 0 to 0.2 wt. % Cr, 0 to 0.2 wt. % Zn, 0 to 0.1 wt. % Ti, and up to 0.15 wt. % of impurities, and Al, wherein the aluminum alloy comprises a yield strength from 200 MPa to 350 MPa in an Hxx temper, and wherein the tensile elongation of the aluminum alloy is greater than 7.5%.
2. The aluminum alloy of claim 1 , comprising 0 to 0.05 wt. % Si, 0 to 0.1 wt. % Fe, 0.01 to 0.1 wt. % Cu, 0.35 to 0.5 wt. % Mn, 2.0 to 3.5 wt. % Mg, 0 to 0.1 wt. % Cr, 0 to 0.1 wt. % Zn, 0 to 0.05 wt. % Ti, and up to 0.15 wt. % of impurities, and Al.
3. The aluminum alloy of claim 2 , comprising 0.01 to 0.05 wt. % Si, 0.01 to 0.08 wt. % Fe, 0.01 to 0.05 wt. % Cu, 0.4 to 0.5 wt. % Mn, 3.0 to 3.5 wt. % Mg, 0.001 to 0.05 wt. % Cr, 0.001 to 0.05 wt. % Zn, 0.001 to 0.03 wt. % Ti, and up to 0.15 wt. % of impurities, and Al.
4. A product comprising the aluminum alloy according to claim 1 .
5. The product of claim 4 , wherein the product is a sheet.
6. The product of claim 5 , wherein the sheet is an anodized sheet.
7. The product of claim 6 , wherein one or more surfaces of the anodized sheet comprises a 60° gloss value from 60 to 100.
8. The product of claim 6 , wherein one or more surfaces of the anodized sheet comprises an 1 value from 60 to 90, an a value from −2 to 2, and/or a b value from −2 to 2, as measured by Hunter L, a, b color scale.
9. The product of claim 5 , wherein one or more surfaces of the sheet comprises a surface roughness value from 0.1 μm to 0.35 μm.
10. The product of claim 6 , wherein one or more surfaces of the anodized sheet comprises a surface roughness value from 0.2 μm to 0.8 μm.
11. The product of claim 4 , wherein the product comprises a consumer electronic part or a consumer electronic product part.
12. The product of claim 4 , wherein the product comprises an architectural sheet product or an architectural sheet product part.
13. The product of claim 4 , wherein the product comprises an automobile body part.
14. A method of producing an aluminum product, comprising:
casting an aluminum alloy to form a cast aluminum alloy, wherein the aluminum alloy comprises 0 to 0.1 wt. % Si, 0 to 0.19 wt. % Fe, 0.01 to 0.3 wt. % Cu, 0.35 to 0.5 wt. % Mn, 2.0 to 3.5 wt. % Mg, 0 to 0.2 wt. % Cr, 0 to 0.2 wt. % Zn, 0 to 0.1 wt. % Ti, and up to 0.15 wt. % of impurities, and Al;
scalping the cast aluminum alloy;
homogenizing the cast aluminum alloy;
hot rolling the cast aluminum alloy to produce a rolled product; and
cold rolling the rolled product,
wherein the aluminum alloy comprises a yield strength from 200 MPa to 350 MPa in an Hxx temper; and
wherein the tensile elongation of the aluminum alloy is greater than 7.5%.
15. The method of claim 14 , further comprising annealing the rolled product after the cold rolling step.
16. The method of claim 14 , wherein the cold rolling step is a two-stage cold rolling step, wherein the two-stage cold rolling step comprising a first cold rolling step, an intervening annealing step, and a second cold rolling step.
17. An aluminum alloy product, wherein the aluminum alloy product is prepared by the method of claim 14 .