GLASS RESIN LAMINATE
A glass resin laminate includes a sheet glass having a compressive stress layer formed in a main surface thereof and a resin layer provided on the sheet glass. A surface compressive stress in the main surface of the sheet glass is 200 MPa or more. A depth of the compressive stress layer is 3 μm or more. A central tension CT (MPa) and a sheet thickness t (mm) of the sheet glass satisfy the equations CT≤64.1× t −0.703 (4) and CT>−38.7×ln(t)+48.2 (5).
1 . A glass resin laminate comprising a sheet glass having a compressive stress layer formed in a main surface thereof and a resin layer provided on the sheet glass, wherein
a surface compressive stress in the main surface of the sheet glass is 200 MPa or more, a depth of the compressive stress layer is 3 μm or more, and a central tension CT (MPa) and a sheet thickness t (mm) of the sheet glass satisfy the following equations (4) and (5):
CT≤64.1× t −0.703 (4)
CT>−38.7×ln( t )+48.2 (5).
2 . The glass resin laminate according to claim 1 , wherein a Young's modulus of the resin layer is 0.01 to 10 MPa.
3 . The glass resin laminate according to claim 1 , wherein an adhesion of the resin layer to the sheet glass is 10 to 1,000 N/m 2 .
4 . The glass resin laminate according to claim 1 , wherein a safety index of the sheet glass is 2 or more.
5 . The glass resin laminate according to claim 1 , which is used for an electronic instrument including a liquid crystal display device and disposed for use such that the resin layer intervenes between the sheet glass and the liquid crystal display device.