Process for reducing lint from tissue and towel products
A method of making a tissue or paper towel product including forming two or more multi-layered webs of cellulosic fibers by a papermaking process using a structured fabric, the papermaking process comprising a step of adding a cross-linker to a pulp slurry comprising the cellulosic fibers so that at least some of the cellulosic fibers are cross-linked within the pulp slurry, and laminating the two or more multi-layered webs together so as to form a multi-ply product, each ply of the multi-ply product comprising cross-linked fibers as a percentage of the total fiber mix of the ply.
1. A method of making a tissue or paper towel product comprising:
forming two or more multi-layered webs of cellulosic fibers by a papermaking process using a structured fabric, the papermaking process comprising a step of adding a cross-linker and micro-fibrillated cellulose to a pulp slurry comprising the cellulosic fibers so that at least some of the cellulosic fibers are cross-linked with one another and with the micro-fibrillated cellulose by the cross-linker within the pulp slurry; and
laminating the two or more multi-layered webs together so as to form a multi-ply product, each ply of the multi-ply product comprising cross-linked fibers as a percentage of the total fiber mix of the ply,
wherein the micro-fibrillated cellulose is added at an inclusion rate of 0.5 to 2 wt % based on oven dry weight of a total amount of pulp fiber in the tissue or paper towel product.
2. The method of claim 1 , wherein the pulp slurry further comprises water and a binder.
3. The method of claim 2 , wherein consistency of the pulp slurry is between 2% to 6%.
4. The method of claim 2 , wherein consistency of the pulp slurry is between 3% to 5%.
5. The method of claim 2 , wherein the cross-linker is a glyoxal-containing cross-linker.
6. The method of claim 2 , wherein the binder is a cationic starch containing 0.2% to 0.6% nitrogen by weight.
7. The method of claim 2 , wherein the pulp slurry is mixed in a vessel with agitation from 5 to 45 minutes between 150 to 200 degrees Fahrenheit to produce the cross-linked fibers.
8. The method of claim 2 , wherein the pulp slurry is mixed in a vessel with agitation from 5 to 30 minutes between 165 and 180 degrees Fahrenheit to produce the cross-linked fibers.
9. The method of claim 2 , wherein the cross-linked fibers are blended in different ratios into stock chests that supply different layers of a multi-layered stock preparation system comprising a multi-layered headbox.
10. The method of claim 2 , wherein the cross-linked fibers are blended only into stock chests which feed a layer configured to face outward when the webs of the tissue or towel product are laminated together.
11. The method of claim 2 , wherein the cross-linked fibers are blended only into stock chests which feed a layer configured to face outward when the webs of the tissue or towel product are laminated together, and the cross-linked fibers make up less than 50% of the total weight percentage of that layer.
12. The method of claim 1 , wherein the tissue or paper towel product is made using a process selected from the group consisting of: Through Air Drying (TAD), Uncreped Through Air Drying (UCTAD), Advanced Tissue Molding System (ATMOS), New Tissue Technology (NTT) and Energy Efficient Technologically Advanced Drying (ETAD).
13. The method of claim 1 , wherein consistency of the pulp is between 2% to 6%.
14. The method of claim 1 , wherein consistency of the pulp is between 3% to 5%.
15. The method of claim 1 , wherein the micro-fibrillated cellulose is added at a consistency of 0% to 3%.
16. The method of claim 1 , wherein the micro-fibrillated cellulose is added at a consistency of 1%.
17. The method of claim 1 , wherein the cross linker that cross-links the at least some of the cellulosic fibers with the micro-fibrillated cellulose is a glyoxal-containing cross-linker added in an amount of 0.05 wt % to 0.25 wt % based on the oven dry weight of the pulp fiber.
18. The method of claim 1 , wherein the pulp slurry further comprises a binder and the binder is a cationic starch containing 0.2 wt % to 0.6 wt % nitrogen, added between 25 to 200 dry lbs per metric ton of oven dry weight of the pulp fiber.
19. The method of claim 1 , wherein the pulp slurry is mixed in a vessel with agitation from 5 to 45 minutes between 150 to 200 degrees Fahrenheit to produce the cellulose fibers cross-linked with one another and with the microfibrillated cellulose.
20. The method of claim 1 , wherein the pulp slurry is mixed in a vessel with agitation from 5 to 30 minutes between 165 and 180 degrees Fahrenheit to produce the cellulose fibers cross-linked with one another and with the microfibrillated cellulose.
21. The method of claim 1 , wherein the cellulose fibers cross-linked with one another and with the micro-fibrillated cellulose are blended in different ratios into stock chests that supply different layers of a multilayered stock preparation system.
22. The method of claim 1 , wherein the cellulose fibers cross-linked with one another and with the micro-fibrillated cellulose are blended only into stock chests which feed a layer configured to face outward when the webs of the tissue or towel product are laminated together.
23. The method of claim 1 , wherein the cellulose fibers cross-linked with one another and with the micro-fibrillated cellulose are blended only into stock chests which feed a layer configured to face outward when the webs of the tissue or towel product are laminated together and the cross-linked fiber is less than 50 wt % of the total weight percentage of that layer.
24. The method of claim 1 , further comprising the step of mixing the micro-fibrillated cellulose with a chemical strength agent before adding the micro-fibrillated cellulose to the pulp slurry.
25. The method of claim 24 , wherein the chemical strength agent and micro-fibrillated cellulose are mixed and diluted to a total solids content between 0.5% to 3.0% with continuous agitation.
26. The method of claim 24 , wherein the chemical strength agent mixed with micro-fibrillated cellulose is added such that the mixture is between 0.5 wt % to 10 wt % total of the bone dry web.
27. The method of claim 24 , wherein the chemical strength agent mixed with micro-fibrillated cellulose is added to a stock system such that all layers of a multi-layer headbox are infused with the mixture.
28. The method of claim 24 , wherein the chemical strength agent mixed with micro-fibrillated cellulose is added only into stock chests which feed the layer of a multilayered headbox configured to face outward when the webs of the tissue or towel product are laminated together.