Method for producing positive electrode for secondary battery
The present disclosure relates to a method for producing a positive electrode for a secondary battery, the method including applying a composition for forming a positive electrode on a positive electrode current collector to form a positive electrode mixture layer, and rolling the positive electrode mixture layer such that the elongation of the positive electrode current collector is less than 1%, to produce a positive electrode.
1. A method for producing a positive electrode for a secondary battery, the method comprising:
applying a composition for forming the positive electrode on a positive electrode current collector to form a positive electrode mixture layer; and
rolling the positive electrode mixture layer such that the elongation of the positive electrode current collector is less than 1%, to produce the positive electrode,
wherein the elongation is a weight reduction ratio per 1.4875 cm 2 area and 20 μm thickness of the current collector after rolling compared to before rolling.
2. The method of claim 1 , wherein the rolling is performed two times or less.
3. The method of claim 1 , wherein after the rolling, the porosity of the positive electrode mixture layer is 25% or less.
4. The method of claim 1 , wherein the rolling is performed at a pressure of 3 to 5 kgf.
5. The method of claim 1 , wherein the positive electrode current collector before the rolling has an area of 1.4875 cm 2 and a weight per 20 μm thickness of 8.0 to 9.0 mg.
6. The method of claim 1 , wherein the composition for forming a positive electrode comprises a positive active material, a conductive material, and a binder,
wherein the positive electrode active material has an average particle diameter (D 50 ) of 5 to 15 μm.
7. The method of claim 1 , wherein the composition for forming the positive electrode comprises a positive active material, a conductive material, and a binder,
wherein the positive electrode active material comprises large-diameter particles having an average particle diameter (D 50 ) of 15 to 25 μm and small-diameter particles having an average particle diameter (D 50 ) of 3 to 6 μm.
8. The method of claim 7 , wherein the large-diameter particles and the small-diameter particles are mixed at a weight ratio of 9:1 to 7:3.
9. The method of claim 1 , wherein the positive electrode current collector is at least one selected from the group consisting of nickel, titanium, sintered carbon, and stainless steel.
10. The method of claim 1 , wherein the composition for forming the positive electrode comprises a positive electrode active material, a conductive material and a binder,
wherein the positive electrode active material is a lithium transition metal oxide comprising at least one selected from the group consisting of nickel (Ni), cobalt (Co), and manganese (Mn).