Polysaccharide fibers and method for producing same
The present invention relates to a method for the production of polysaccharide fibers which contain α(1→3)-glucan as a fiber-forming substance, as well as to the fibers made thereby, and to their use.
1. A method of producing a polysaccharide fiber whose fiber-forming substance is α(1→3)-glucan, wherein the method comprises:
(i) preparing a spinning solution comprising α(1→3)-glucan, sodium hydroxide, and carbon disulfide (CS 2 ), wherein there is about 5% to about 7.5% by weight CS 2 relative to the α(1→3)-glucan, and
(ii) extruding the spinning solution to produce the polysaccharide fibers.
2. The method according to claim 1 , wherein at least 90% of the α(1→3)-glucan are hexose units and at least 50% of the hexose units are linked via α(1→3)-glycosidic bonds.
3. The method according to claim 1 , wherein the fiber is a staple fiber or a continuous filament.
4. The method according to claim 1 , wherein step (i) comprises first preparing a solution comprising the α(1→3)-glucan and the sodium hydroxide, and then admixing the CS 2 to prepare the spinning solution.
5. The method according to claim 1 , further comprising (iii) stretching the polysaccharide fiber.
6. The method according to claim 1 , wherein the weight-average degree of polymerization (DPw) of the α(1→3)-glucan is between 200 and 2000.
7. The method according to claim 6 , wherein the DPw of the α(1→3)-glucan is between 500 and 1000.