Substrates for the attachment of molecules
A substrate comprising a coating of a masking material, and a plurality of discrete reaction zones onto which one or more binding agents are intended to be attached, wherein said zones are uncoated areas on the substrate.
1. A substrate comprising a coating of a masking material and a plurality of discrete reaction zones onto which one or more binding agents are intended to be attached, wherein said zones are uncoated areas on the substrate wherein the masking material comprises a pigment, an acrylic resin, an epoxy resin and a structuring agent, wherein
the pigment is present in an amount of 1 to 8% w/w of the masking composition,
the epoxy resin is present in an amount of 15 to 50% w/w of the masking composition,
the acrylic resin is present in an amount of 2 to 10% w/w of the masking composition, and
the structuring agent is present in an amount of 15-50% w/w of the masking composition.
2. A substrate of claim 1 , wherein the masking material has a contact angle of 60-120°.
3. A substrate according to claim 2 , wherein the contact angle is 90° -120°.
4. A substrate according to claim 1 , wherein the substrate is approximately 100 mm×99 mm in size, and wherein the substrate comprises square subsections that are approximately 9 mm×9 mm in size, each square subsection comprising a grid of discrete reaction zones, and wherein each square section comprises a grid of from 5×5, 10×10, 20×20, or 30×30discrete reaction zones.
5. A substrate according to claim 1 , wherein the density of the discrete reaction zones is in the range of from 0.08 to 15 zones/mm 2 .
6. A substrate according to claim 1 , wherein each discrete reaction zone has a diameter ranging from 0.1 mm to 1 mm in diameter.
7. A substrate according to claim 1 , comprising one or more binding agents immobilised on the discrete reaction zones.
8. A substrate according to claim 1 , wherein the substrate comprises silicon, metal oxides, ceramic, glass or plastic.
9. A substrate according to claim 1 , wherein the thickness of the coating applied to the substrate is 2 to 50 μm (micron) thick.
10. A substrate according to claim 1 , wherein the coating of masking material is a color ranging from off-white to black.
11. A substrate according to claim 1 , wherein the discrete reaction zones are chemically activated to allow immobilisation of binding agent.
12. A substrate according to claim 1 , wherein
the pigment is present in an amount of about 5% w/w of the masking composition;
the epoxy resin is present in an amount of about 30% w/w of the masking composition,
the acrylic resin is present in an amount of about 10% w/w of the masking composition, and
the structuring agent is present in an amount of about 20% w/w of the masking composition.
13. A substrate according to claim 1 , wherein the binding agents are antibodies.