Stator compound having an NBIR terpolymer elastomeric base and stators and downhole motors using the same

1. A method of making a stator compound, comprising:

during a first mixing stage, mixing a high reinforcing carbon black with an elastomeric base at a temperature below about 300 degrees Fahrenheit without curing agents to produce a mixture, wherein the elastomeric base has one or more rubber components, wherein the only rubber components of the elastomeric base are acrylonitrile butadiene isoprene rubbers (NBIR); and

during a second mixing stage, mixing curing agents into the mixture.

2. The method of claim 1 , wherein mixing a high reinforcing carbon black with the elastomeric base comprises mixing a high reinforcing carbon black having a surface area of about 80 to about 250 (Iodine # mg/g) and a structure of about 70 to about 178 (DOP Absorption—cc/100 g) with the elastomeric base.

3. The method of claim 1 , further comprising mixing a semi-reinforcing carbon black with the elastomeric base during the first mixing stage.

4. The method of claim 3 , wherein mixing a semi-reinforcing carbon black with the elastomeric base comprises mixing a semi-reinforcing carbon black having a surface area of about 20 to about 50 (Iodine # mg/g) and a structure of about 60 to about 125 (DOP Absorption—cc/100 g) with the elastomeric base.

5. The method of claim 1 , further comprising mixing at least one plasticizer selected from the group consisting of polymeric and ester plasticizers with the elastomeric base during the first mixing stage.

6. The method of claim 1 , wherein mixing curing agents into the mixture comprises mixing sulfur into the mixture during the second mixing stage.

7. The method of claim 1 , further comprising mixing an antioxidant with the elastomeric base during the first mixing stage.

8. The method of claim 1 , further comprising mixing at least one of a phenolic resin without a curing agent, zinc oxide, stearic acid, and hexamethylene tetraamine with the elastomeric base during the first mixing stage.

9. A stator for use in a downhole motor or pump and having a stator liner, the stator liner formed of a stator compound having an elastomeric base, the elastomeric base having one or more rubber components, wherein the only rubber components of the elastomeric base are acrylonitrile butadiene isoprene rubbers (NBIR).

10. The stator of claim 9 , wherein the rubber components are selected from the group consisting of hydrogenated acrylonitrile butadiene isoprene rubber (HNBIR), acrylonitrile butadiene isoprene rubber that has not been hydrogenated, and carboxylated acrylonitrile butadiene isoprene rubber (XNBIR).

11. The stator of claim 9 , wherein the stator liner is formed of a stator compound further including a least one of a high reinforcing carbon black and a semi-reinforcing carbon black.

12. The stator of claim 9 , wherein the stator liner is formed of a stator compound further including a high reinforcing carbon black having a surface area of about 80 to about 250 (Iodine # mg/g) and a structure of about 70 to about 178 (DOP Absorption—cc/100 g).

13. The stator of claim 9 , wherein the stator liner is formed of a stator compound further including a semi-reinforcing carbon black has a surface area of about 20 to about 50 (Iodine # mg/g) and a structure of about 60 to about 125 (DOP Absorption—cc/100 g).

14. The stator of claim 9 , wherein the stator liner is formed of a stator compound further including at least one plasticizer selected from the group consisting of polymeric and ester plasticizers.

15. The stator of claim 9 , wherein the stator liner is formed of a stator compound further including an antioxidant.