Elastomer composition having a very good dispersion of the charge in the elastomer matrix
View Patent ↗The invention relates to a rubber composition based on at least one diene elastomer, a reinforcing filler including at least carbon black, having a specific surface area CTAB greater than or equal to 130 m 2 /g, a plasticizing hydrocarbon resin, the vitreous transition temperature of which, Tg, is greater than 20° C., and the softening point of which is less than 170° C., and a cross linking system, the dispersion of the filler in the elastomeric matrix having a Z score greater than or equal to 70.
1. A process for preparing a composition comprising:
at least one diene elastomer,
a reinforcing filler comprising at least carbon black having a CTAB specific surface area greater than or equal to 130 m 2 /g,
a plasticizing hydrocarbon resin having a glass transition temperature, Tg, which is greater than 20° C. and a softening point which is less than 170° C., and
a crosslinking system,
wherein the reinforcing filler is dispersed in the composition such that the dispersion of the reinforcing filler in the composition has a Z score greater than or equal to 70,
which comprises:
preparing a first masterbatch comprising the at least one diene elastomer and the carbon black, and the first masterbatch exhibiting a dispersion of the carbon black in a matrix including the at least one diene elastomer which has a Z score greater than or equal to 80,
incorporating the first masterbatch and the plasticizing hydrocarbon resin in a mixer to form a mixture, and thermomechanically kneading the mixture until a maximum temperature of between 130° C. and 200° C. is reached,
cooling the mixture to a temperature of less than 100° C.,
subsequently incorporating the crosslinking system into the mixture,
kneading the mixture until a maximum temperature of less than 120° C. is reached.
2. The process according to claim 1 , wherein the first masterbatch is produced in a liquid phase from at least one diene elastomer latex and a dispersion of the carbon black.
3. The process according to claim 2 , wherein the first masterbatch is produced by:
feeding a continuous stream of the at least one diene elastomer latex to a mixing zone of a coagulation reactor defining an elongate coagulation zone extending between the mixing zone and an outlet orifice,
feeding a continuous stream of a fluid comprising the carbon black under pressure to the mixing zone of a coagulation reactor to form a coagulum,
drying the coagulum, thereby recovering the first masterbatch.
4. The process according to claim 1 , wherein the at least one diene elastomer is selected from the group consisting of polybutadienes, natural rubber, synthetic polyisoprenes, butadiene copolymers, isoprene copolymers, and blends of these elastomers.
5. The process according to claim 4 , wherein the at least one diene elastomer includes a natural rubber.
6. The process according to claim 1 , wherein the content of carbon black ranges from 20 to 80 parts per hundred parts by weight of elastomer.
7. The process according to claim 1 , wherein the content of plasticizing resin ranges from 2 to 35 parts per hundred parts by weight of elastomer.
8. The process according to claim 1 , further comprising introducing an inorganic filler and/or a second elastomer into the mixture in the mixer simultaneously with the first masterbatch and the plasticizing hydrocarbon resin.
9. The process according to claim 1 , further comprising introducing an inorganic filler and a second elastomer into the mixture in the mixer in the form of a specific masterbatch prepared beforehand.
10. The process according to claim 1 , further comprising introducing an inorganic filler and a second elastomer separately into the mixture in the mixer, the inorganic filler being introduced before or after the second elastomer.
11. The process according to claim 10 , wherein the introduction of the inorganic filler and of the second elastomer is offset in time by a few tens of seconds to a few minutes relative to the introduction of the first masterbatch comprising the at least one diene elastomer and the carbon black into the mixer.
12. A masterbatch based on: at least one diene elastomer, reinforcing filler comprising at least carbon black having a CTAB specific surface area greater than or equal to 130 m 2 /g, a plasticizing hydrocarbon resin, having a glass transition temperature, Tg, which is greater than 20° C. and a softening point which is less than 170° C., wherein the reinforcing filler is dispersed in a matrix including the at least one diene elastomer and the plasticizing hydrocarbon resin such that the dispersion has a Z score greater than or equal to 70.
13. The masterbatch according to claim 12 , which is obtained from a first masterbatch comprising the at least one diene elastomer and the carbon black, and wherein the dispersion of the carbon black in a matrix including the at least one diene elastomer of the first masterbatch has a Z score greater than or equal to 80.
14. A masterbatch based on: at least one diene elastomer, a reinforcing filler comprising at least carbon black having a CTAB specific surface area greater than or equal to 130 m 2 /g, a plasticizing hydrocarbon resin, having a glass transition temperature, Tg, which is greater than 20° C. and a softening point which is less than 170° C., which is obtained from a first masterbatch comprising the at least one diene elastomer and the carbon black, and wherein the dispersion of the carbon black in a matrix including the at least one diene elastomer of the first masterbatch has a Z score greater than or equal to 80.
15. The masterbatch according to claim 14 , wherein the first masterbatch is obtained by mixing in a liquid phase from a diene elastomer latex and an aqueous dispersion of carbon black.
16. A tire or semi-finished product comprising at least one composition made by the process according to claim 1 .
17. A tire or semi-finished product comprising a masterbatch according to claim 12 .
18. A tire or semi-finished product comprising a masterbatch according to claim 14 .