Aqueous dispersion and coating material using the same, and photocatalytic film and product
An aqueous dispersion of an embodiment includes visible-light responsive photocatalytic composite microparticles containing tungsten oxide and zirconium oxide, and an aqueous dispersion medium in which the photocatalytic composite microparticles are dispersed. In the photocatalytic composite microparticles, a ratio of a mass of the zirconium oxide to a mass of the tungsten oxide is in a range of from 0.05% to 200%, and a D50 particle size in particle size distribution is in a range of from 20 nm to 10 μm. The aqueous dispersion has pH in a range of from 1 to 9.
1. A method for manufacturing a photocatalytic film, comprising:
preparing an aqueous dispersion including a visible-light responsive photocatalytic composite microparticles containing tungsten oxide microparticles and zirconium oxide microparticles, and an aqueous dispersion medium in which the photocatalytic composite microparticles are dispersed; and
applying the aqueous dispersion on a base material to form a photocatalytic film having a film thickness in a range of 2 to 1000 nm,
wherein the photocatalytic composite microparticles are dispersed in the aqueous dispersion medium in a range of 0.001 to 50 mass %;
wherein a D50 particle size in a particle size distribution of the photocatalytic composite microparticles is in a range of 20 nm to 10 μm;
wherein the zirconium oxide microparticles have rod-shaped primary particles, and a ratio of an average major axis of the rod-shaped primary particles to an average primary particle size of the tungsten oxide microparticles is in a range of 0.05 to 20; and
wherein a pH of the aqueous dispersion is in a range of 1 to 9.
2. The method according to claim 1 ,
wherein the photocatalytic composite microparticles contain at least one metal element selected from the group consisting of nickel, titanium, manganese, iron, palladium, platinum, ruthenium, copper, silver, aluminum, and cerium; and
wherein the photocatalytic composite microparticles contain the zirconium oxide microparticles in a range of 10 to 200 mass % with respect to the tungsten oxide microparticles, the metal element in a range of 0.005 to 2 mass % with respect to the tungsten oxide microparticles, and the balance being the tungsten oxide microparticles.
3. The method according to claim 1 ,
wherein the D50 particle size of the photocatalytic composite microparticles is in a range of 50 nm to 1 μm; and
wherein the pH of the aqueous dispersion is in a range of 5 to 7.5.
4. The method according to claim 1 ,
wherein a D90 particle size in a particle size distribution of the photocatalytic composite microparticles is in a range of 0.05 to 10 μm.
5. The method according to claim 1 ,
wherein the aqueous dispersion contains at least one selected from the group consisting of activated carbon, zeolite, and porous ceramics.
6. The method according to claim 1 ,
wherein the base material is made of glass, ceramics, resin, metal, paper, fiber, or wood.
7. The method according to claim 1 ,
wherein the photocatalytic film is formed on a surface of a building material, an interior material, a home electric appliance, or a filter used in a home electric appliance.
8. A method for manufacturing a photocatalytic film, comprising:
preparing a coating material comprising: an aqueous dispersion including a visible-light responsive photocatalytic composite microparticles containing tungsten oxide microparticles and zirconium oxide microparticles, and an aqueous dispersion medium in which the photocatalytic composite microparticles are dispersed; and a binder component comprising at least one selected from the group consisting of an inorganic binder and an organic binder; and
applying the coating material on a base material to form a photocatalytic film having a film thickness in a range of 2 to 1000 nm,
wherein the photocatalytic composite microparticles are dispersed in the aqueous dispersion medium in a range of 0.001 to 50 mass %;
wherein a D50 particle size in a particle size distribution of the photocatalytic composite microparticles is in a range of 20 nm to 10 μm;
wherein the zirconium oxide microparticles have rod-shaped primary particles, and a ratio of an average major axis of the rod-shaped primary particles to an average primary particle size of the tungsten oxide microparticles is in a range of 0.05 to 20; and
wherein a pH of the aqueous dispersion is in a range of 1 to 9.
9. The method according to claim 8 ,
wherein the photocatalytic composite microparticles contain at least one metal element selected from the group consisting of nickel, titanium, manganese, iron, palladium, platinum, ruthenium, copper, silver, aluminum, and cerium; and
wherein the photocatalytic composite microparticles contain the zirconium oxide microparticles in a range of 10 to 200 mass % with respect to the tungsten oxide microparticles, the metal element in a range of 0.005 to 2 mass % with respect to the tungsten oxide microparticles, and the balance being the tungsten oxide microparticles.
10. The method according to claim 8 ,
wherein the D50 particle size of the photocatalytic composite microparticles is in a range of 50 nm to 1 μm; and
wherein the pH of the aqueous dispersion is in a range of 5 to 7.5.
11. The method according to claim 8 ,
wherein a D90 particle size in a particle size distribution of the photocatalytic composite microparticles is in a range of 0.05 to 10 μm.
12. The method according to claim 8 ,
wherein the coating material contains at least one selected from the group consisting of activated carbon, zeolite, and porous ceramics.
13. The method according to claim 8 ,
wherein the base material is made of glass, ceramics, resin, metal, paper, fiber, or wood.
14. The method according to claim 8 ,
wherein a content of the binder component in the coating material is in a range of from 5 to 95 mass %.
15. The method according to claim 8 ,
wherein the inorganic binder comprises at least one selected from the group consisting of a product obtained through decomposition of a hydrolytic silicon compound, an organopolysiloxane compound, a polycondensate of the organopolysiloxane compound, silica, water glass, phosphate, metal oxide, cement, gypsum, lime, and frit.
16. The method according to claim 8 ,
wherein the organic binder comprises at least one selected from the group consisting of fluorine-based resin, silicone resin, acrylic resin, epoxy resin, polyether resin, melamine resin, urethane resin, and alkyd resin.
17. The method according to claim 8 ,
wherein the photocatalytic film is formed on a surface of a building material, an interior material, a home electric appliance, or a filter used in a home electric appliance.