SOLAR CELL
A solar cell includes a silicon substrate and an electrode on the silicon substrate. The silicon substrate includes at least 5 raised portions having a cross-sectional height (h) of about 50 nm or more per 5 μm length. The electrode is formed from a composition for solar cell electrodes having a water contact angle of about 15° to about 60°.
1 . A solar cell, comprising:
a silicon substrate and an electrode on the silicon substrate,
wherein the silicon substrate includes at least 5 raised portions having a cross-sectional height (h) of about 50 nm or more per 5 μm length, and
the electrode is formed from a composition for solar cell electrodes having a water contact angle of about 15° to about 60°.
2 . The solar cell according as claimed in claim 1 , wherein the composition for solar cell electrodes includes:
about 60 wt % to about 95 wt % of a conductive powder;
about 0.1 wt % to about 20 wt % of a glass frit;
about 0.1 wt % to about 15 wt % of an organic binder;
about 0.1 wt % to about 5 wt % of a surface tension modifier; and
about 0.1 wt % to about 20 wt % of a solvent.
3 . The solar cell according as claimed in claim 2 , wherein the glass frit includes at least one elemental metal of tellurium (Te), lithium (Li), zinc (Zn), bismuth (Bi), lead (Pb), sodium (Na), phosphorus (P), germanium (Ge), gallium (Ga), cerium (Ce), iron (Fe), silicon (Si), tungsten (W), magnesium (Mg), molybdenum (Mo), cesium (Cs), strontium (Sr), titanium (Ti), tin (Sn), indium (In), vanadium (V), barium (Ba), nickel (Ni), copper (Cu), potassium (K), arsenic (As), cobalt (Co), zirconium (Zr), manganese (Mn), aluminum (Al), and boron (B).
4 . The solar cell according as claimed in claim 2 , wherein the surface tension modifier includes at least one of a silicone-based additive, an amide-based additive, and a fatty acid-based surfactant.
5 . The solar cell according as claimed in claim 2 , wherein the solvent includes at least one of hexane, toluene, ethyl cellosolve, cyclohexanone, butyl cellosolve, butyl carbitol (diethylene glycol monobutyl ether), dibutyl carbitol (diethylene glycol dibutyl ether), butyl carbitol acetate (diethylene glycol monobutyl ether acetate), propylene glycol monomethyl ether, hexylene glycol, methylethylketone, benzyl alcohol, γ-butyrolactone, ethyl lactate, texanol, and diethylene glycol dibutyl ether.
6 . The solar cell according as claimed in claim 2 , wherein the organic binder includes at least one of ethyl hydroxyethyl cellulose, nitrocellulose, a blend of ethyl cellulose and phenol resins, an alkyd resin, a phenol resin, an acrylate ester resin, a xylene resin, a polybutane resin, a polyester resin, a urea resin, a melamine resin, a vinyl acetate resin, wood rosin, a polymethacrylate of an alcohol, polyvinyl butyrate, and polyvinyl acetal.
7 . The solar cell according as claimed in claim 2 , wherein the composition for solar cell electrodes further includes at least one additive, the at least one additive including at least one of a dispersant, a thixotropic agent, a plasticizer, a viscosity stabilizer, an anti-foaming agent, a pigment, a UV stabilizer, an antioxidant, and a coupling agent.