Polyamide nanofiber nonwovens
A nanofiber nonwoven product is disclosed which comprises a polyamide with a relative viscosity from 2 to 330, spun into nanofibers with an average diameter of less than 1000 nanometers (1 micron). In general, the inventive products are prepared by: (a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 2 to 330; (b) melt spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter of less than 1 micron, followed by (c) forming the nanofibers into the product.
1. A nanofiber nonwoven product comprising polyamide nanofibers, wherein the polyamide of the nanofibers comprises at least one of N6, N66, N6T/66, N612, N6/66, N6I/66, N66/6I/6T, N11, N12, or combinations thereof, wherein “N” means Nylon, wherein the polyamide of the nanofibers has a relative viscosity from 4 to 330, and wherein the nanofibers have an average diameter from 100 to 950 nanometers.
2. The nanofiber nonwoven product according to claim 1 , wherein the melt point of the product is 225° C. or greater.
3. The nanofiber nonwoven product according to claim 1 , wherein no more than 20% of the nanofibers have a diameter of greater than 700 nanometers.
4. The nanofiber nonwoven product according to claim 1 , wherein the polyamide of the nanofibers comprises nylon 66 or nylon 6/66.
5. The nanofiber nonwoven product according to claim 1 , wherein the polyamide of the nanofibers is a high temperature nylon.
6. The nanofiber nonwoven product according to claim 1 , wherein the product has an Air Permeability Value of less than 600 CFM/ft 2 .
7. The nanofiber nonwoven product according to claim 1 , wherein the product has a basis weight of 150 GSM or less.
8. The nanofiber nonwoven product according to claim 1 , wherein the product has a TDI of at least 20 ppm and an ODI of at least 1 ppm.
9. The nanofiber nonwoven product according to claim 1 , wherein the product is free of solvent.
10. The nanofiber nonwoven product according to claim 1 , wherein the product comprises less than 5000 ppm solvent.
11. A nanofiber nonwoven product comprising a polyamide which is spun into nanofibers with an average diameter from 100 to 950 nanometers and formed into said nonwoven product, wherein the polyamide of the nanofibers comprises at least one of N6, N66, N6T/66, N612, N6/66, N6I/66, N66/6I/6T, N11, N12, or combinations thereof, wherein “N” means Nylon, wherein the polyamide has a relative viscosity from 4 to 330.
12. A method of making a nanofiber nonwoven product, the method comprising:
(a) providing a polyamide composition, wherein the polyamide has a relative viscosity from 4 to 330 wherein the polyamide of the nanofibers comprises at least one of N6, N66, N6T/66, N612, N6/66, N6I/66, N66/6I/6T, N11, N12, or combinations thereof, wherein “N” means Nylon;
(b) spinning the polyamide composition into a plurality of nanofibers having an average fiber diameter from 100 to 1000 nanometers and a relative viscosity from 4 to 330; and
(c) forming the nanofibers into the nanofiber nonwoven product, wherein the polyamide nanofiber layer has an average nanofiber diameter from 100 to 950.
13. The method of making the nanofiber nonwoven product according to claim 12 , wherein the moisture content of the polyamide composition is from 10 ppm to 5 wt. %.
14. The method of making the nanofiber nonwoven product according to claim 13 , wherein the relative viscosity of the polyamide in the nanofiber nonwoven product is the same or increased as compared to the polyamide composition prior to spinning and forming the product.
15. The method of making the nanofiber nonwoven product according to claim 12 , wherein the polyamide composition is melt spun by way of melt-blowing through a die into a high velocity gaseous stream.
16. The method of making the nanofiber nonwoven product according to claim 12 , wherein the polyamide composition is melt-spun by 2-phase propellant-gas spinning, including extruding the polyamide composition in liquid form with pressurized gas through a fiber-forming channel.
17. The method of making the nanofiber nonwoven product according to claim 12 , wherein the nanofiber nonwoven product is formed by collecting the nanofibers on a moving belt.
18. The method of making the nanofiber nonwoven product according to claim 12 , wherein the polyamide nanofiber layer has a basis weight of 150 GSM or less.
19. The method of making the nanofiber nonwoven product according to claim 12 , wherein the relative viscosity of the polyamide in the nanofiber nonwoven product is reduced as compared to the polyamide composition prior to spinning and forming the product.
20. A nanofiber nonwoven product comprising a nylon 66 polyamide which is melt spun into nanofibers and formed into said nonwoven product, wherein the polyamide of the nanofibers has a relative viscosity from 4 to 330, a TDI of at least 20 ppm and an ODI of at least 1 ppm.
21. A nanofiber nonwoven product comprising a nylon 66 polyamide which is melt spun into nanofibers and formed into said nonwoven product, wherein the polyamide of the nanofibers has a relative viscosity from 4 to 330, and wherein no more than 20% of the nanofibers have a diameter of greater than 700 nanometers.