COMPOSITION FOR FORMING SOLAR CELL ELECTRODE AND ELECTRODE FABRICATED USING THE SAME
A composition for solar cell electrodes and a solar cell electrode prepared using the same, the composition including a conductive powder; a glass frit; an organic vehicle; a slip agent; and a thixotropic agent, wherein the composition has an angular velocity of 0.1 rad/sec to 80 rad/sec, as measured for tan δ max under conditions of 23 ° C. and 0.1 rad/sec to 1,000 rad/sec.
1 . A composition for solar cell electrodes, the composition comprising:
a conductive powder;
a glass frit;
an organic vehicle;
a slip agent; and
a thixotropic agent,
wherein the composition has an angular velocity of 0.1 rad/sec to 80 rad/sec, as measured for tan δ max under conditions of 23° C. and 0.1 rad/sec to 1,000 rad/sec.
2 . The composition as claimed in claim 1 , wherein the composition has a tan δ max of about 11 or less, as measured under conditions of 23° C. and 0.1 rad/sec to 1,000 rad/sec.
3 . The composition as claimed in claim 1 , wherein the composition has a storage modulus of about 3,500 Pa or less, as measured under conditions of 23° C. and 1 rad/sec.
4 . The composition as claimed in claim 1 , wherein the organic vehicle includes a first binder resin having a weight average molecular weight of about 20,000 to about 200,000.
5 . The composition as claimed in claim 4 , wherein the organic vehicle further includes a second binder resin having a number average molecular weight of about 500 to about 5,000.
6 . The composition as claimed in claim 5 , wherein:
the first binder resin is present in an amount of about 0.1 wt % to about 20 wt %, based on a total weight of the composition, and
the second binder resin is present in an amount of about 0.1 wt % to about 10 wt %, based on the total weight of the composition.
7 . The composition as claimed in claim 1 , wherein:
the thixotropic agent includes a bisamide thixotropic agent, and
the thixotropic agent is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
8 . The composition as claimed in claim 1 , wherein:
the slip agent includes a linear siloxane or a cyclic siloxane, and
the slip agent is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
9 . The composition as claimed in claim 1 , further comprising a dispersant, wherein the dispersant is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
10 . The composition as claimed in claim 1 , further comprising a plasticizer, a viscosity stabilizer, an anti-foaming agent, a pigment, a UV stabilizer, an antioxidant, or a coupling agent.
11 . A solar cell electrode fabricated using the composition for solar cell electrodes as claimed in claim 1 .
12 . The solar cell electrode as claimed in claim 11 , wherein the composition has a tan δ max of about 11 or less, as measured under conditions of 23° C. and 0.1 rad/sec to 1,000 rad/sec.
13 . The solar cell electrode as claimed in claim 11 , wherein the composition has a storage modulus of about 3,500 Pa or less, as measured under conditions of 23° C. and 1 rad/sec.
14 . The solar cell electrode as claimed in claim 11 , wherein the organic vehicle includes a first binder resin having a weight average molecular weight of about 20,000 to about 200,000.
15 . The solar cell electrode as claimed in claim 14 , wherein the organic vehicle further includes a second binder resin having a number average molecular weight of about 500 to about 5,000.
16 . The solar cell electrode as claimed in claim 15 , wherein:
the first binder resin is present in an amount of about 0.1 wt % to about 20 wt %, based on a total weight of the composition, and
the second binder resin is present in an amount of about 0.1 wt % to about 10 wt %, based on the total weight of the composition.
17 . The solar cell electrode as claimed in claim 11 , wherein:
the thixotropic agent includes a bisamide thixotropic agent, and
the thixotropic agent is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
18 . The solar cell electrode as claimed in claim 11 , wherein:
the slip agent includes a linear siloxane or a cyclic siloxane, and
the slip agent is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
19 . The solar cell electrode as claimed in claim 11 , wherein the composition further includes a dispersant, wherein the dispersant is present in an amount of about 0.1 wt % to about 5 wt %, based on a total weight of the composition.
20 . The solar cell electrode as claimed in claim 11 , wherein the composition further includes a plasticizer, a viscosity stabilizer, an anti-foaming agent, a pigment, a UV stabilizer, an antioxidant, or a coupling agent.
21 . A composition for solar cell electrodes, the composition comprising:
60 wt % to 95 wt % of a conductive powder;
0.1 wt % to 20 wt %, a glass frit;
1 wt % to 30 wt % an organic vehicle, the organic vehicle including a first binder resin having a weight average molecular weight of 20,000 to 200,000 and a second binder resin having a number average molecular weight of 500 to 5,000;
0.1 wt % to 5 wt % of a slip agent, the slip agent including a linear siloxane or a cyclic siloxane; and
0.1 wt % to 5 wt % of a bisamide thixotropic agent, all wt % being based on a total weight of the composition,
wherein the composition has an angular velocity of 0.1 rad/sec to 80 rad/sec, as measured for tan δ max under conditions of 23° C. and 0.1 rad/sec to 1,000 rad/sec.