Method for producing a heat transfer tube for steam generator using drawing, solution heat treatment, and straightening

1. A method for producing a heat transfer tube for a steam generator, the method comprising:

a step of providing a tube;

a step of applying cold drawing to the tube, the step of applying cold drawing to the tube including using a high-pressure lubricating oil that has a pressure of 40 MPa or more;

after the step of applying cold drawing to the tube, a step of applying a solid solution heat treatment to the tube; and

after the step of applying a solid solution heat treatment to the tube, a step of straightening the tube by using a roll straightening machine,

wherein

the roll straightening machine includes at least five pairs of concave globoidal drum type rolls, each pair of rolls being arranged opposite to each other in a vertical direction and in a crossing manner such that directions of rotating shafts of each pair of rolls cross each other, a stand interval being set at 300 mm or less;

in the step of straightening the tube, offsetting is formed by three points along a tube axial centerline that are crossing positions of at least three successive pairs of upper and lower straightening rolls of the roll straightening machine and offsetting makes η expressed by Formula (1) described below to satisfy 0.9×10 −3 or more and ensures an offset amount of 5 mm or less:

η=1/ R ×( d/ 2)  (1)

where given that an outside diameter of the tube is d (mm) and a stand interval of the roll straightening machine is L (mm) and an offset amount is δ (mm), R=(δ 2 +L 2 )/2δ is established.

2. The method for producing a heat transfer tube for a steam generator according to claim 1 , wherein a chemical composition of the tube consists of, in mass %, C: 0.15% or less, Si: 1.00% or less, Mn: 2.0% or less, P: 0.030% or less, S: 0.030% or less, Cr: 10.0 to 40.0%, Ni: 8.0 to 80.0%, Ti: 0.5% or less, Cu: 0.6% or less, Al: 0.5% or less, and N: 0.20% or less, the balance being Fe and impurities.