1. A thermoplastic composition comprising:

2 to 30 wt. % polyamide resin;

up to 40 wt. % modified rosin ester;

up to 40 wt. % modified gum rosin;

0.1 to 10 wt. % pigment;

up to 20 wt. % wax;

less than 10 wt. % plasticizer; and

5 to 90 wt. % of at least one inorganic filler,

wherein the pigment is carbon black.

2. The thermoplastic composition of claim 1 , wherein the modified rosin ester comprises tall oil esters, maleic rosin ester, pentaerythritol rosin ester, glycerol rosin ester, disproportionated rosin ester, hydrogenated rosin, and polymerized rosin.

3. The thermoplastic composition of claim 1 , wherein the wax comprises polyethylene wax.

4. The thermoplastic composition of claim 1 , wherein the plasticizer comprises one or more of castor oil and di-isononyl phthalate.

5. The thermoplastic composition of claim 1 , further comprising:

up to 10 wt. % copolymer;

up to 3 wt. % antioxidant; and

up to 3.5 wt. % light stabilizer.

6. The thermoplastic composition of claim 5 , wherein the copolymer comprises one or more of ethylene vinyl acetate and ethylene maleic anhydride.

7. The thermoplastic composition of claim 5 , wherein the light stabilizer comprises a hindered amine.

8. The thermoplastic composition of claim 1 , wherein the modified gum rosin comprises one or more of glyceryl hydrogenated rosin, rosin modified phenolic resin, pentaerythrityl rosin, glyceryl rosin, disproportionated rosin, polymerized rosin or hydrogenated rosin.

9. The thermoplastic composition of claim 1 , wherein the composition has a viscosity of 1,000 to 50,000 cP, wherein the viscosity is measured at 425° F. with a Brookfield Viscometer at 6 rpm, #4 or #64 spindle.

10. The thermoplastic composition of claim 1 , wherein the composition has a specific gravity of 1.6 to 2.1.

11. The thermoplastic composition of claim 1 , wherein the composition has a hardness of 5 to 75 units measured with 1 kg at 115° F. and shore A durometer.

12. The thermoplastic composition of claim 1 , wherein the composition has softening point of 200° F. to 260° F.

13. The thermoplastic composition of claim 1 , wherein the composition has elongation of at least 20 percent.

14. A thermoplastic composition comprising:

2 to 30 wt. % polyamide resin;

up to 40 wt. % modified rosin ester;

up to 40 wt. % modified gum rosin;

0.1 to 10 wt. % pigment;

up to 20 wt. % wax;

less than 10 wt. % plasticizer; and

5 to 90 wt. % of at least one inorganic filler,

wherein the pigment is carbon black, and

wherein the thermoplastic composition is applied to a roadway comprising a first asphalt and a second asphalt to form a barrier over a longitudinal joint that is substantially parallel to and located between the first asphalt and the second asphalt, wherein the thermoplastic composition seals an edge between the first asphalt and the second asphalt from deterioration.

15. A method of sealing roadway joints with a thermoplastic composition, the method comprising:

adding a wax to a vessel;

adding a polyamide resin to the vessel;

adding a plasticizer to the vessel;

adding at least one of a modified rosin ester or a modified gum rosin to the vessel;

adding a pigment comprising carbon black to the vessel;

adding at least one inorganic filler to the vessel;

mixing the composition;

heating the vessel to 340° F. to 450° F.; and

applying the composition to a roadway to seal a roadway joint.

16. The method of claim 15 , further comprising:

adding a copolymer to the vessel;

adding an antioxidant to the vessel; and

adding a light stabilizer to the vessel.

17. The method of claim 16 , further comprising:

adding a second copolymer to the vessel after the polyamide resin addition.

18. A method of sealing roadway joints, the method comprising:

heating a thermoplastic composition to 340° F. to 450° F.,

wherein the thermoplastic composition comprises:

2 to 30 wt. % polyamide resin;

up to 40 wt. % modified rosin ester;

up to 40 wt. % modified gum rosin;

0.1 to 10 wt. % pigment;

up to 20 wt. % wax;

less than 10 wt. % plasticizer; and

5 to 90 wt. % of at least one inorganic filler,

wherein the thermoplastic composition is mixed during the heating, wherein the mixing is performed by at least one of auger, agitation, or recirculation, and wherein the pigment comprises carbon black; and

applying the heated thermoplastic composition to an asphalt roadway joint of an asphalt roadway, wherein the thermoplastic composition is applied by extruding, spraying, or other application means to the asphalt roadway joint, wherein the asphalt roadway joint comprises a longitudinal joint that is substantially parallel to and located between adjacent lanes of the asphalt roadway.

19. A method of sealing roadway joints comprising:

applying the thermoplastic composition of claim 1 to a roadway to seal a roadway joint.