Aircraft fluid resistant sealant for use on aircraft parts
A number of sealants are provided that are resistant to degradation by aircraft fluids. In some embodiments, the sealants are resistant to degradation by Jet A fluid and at least one of the three types of hydraulic fluids typically used in aircraft. These embodiments are also typically cure in place from a two part polyurethane or polyurea mix, with cure to a visibly clear coating. In some embodiments, they may be sprayed on an aircraft surface or applied by hand (brush or injectable). In other of these embodiments, the sealants comprise, at least in part, a cured, soft, tacky polyurethane gel that is resistant to at least one of a synthetic hydrocarbon based or mineral oil based hydraulic fluid.
1. An assembly for use with a spray gun, the spray gun for applying a sealant coating, the assembly comprising:
a first compartment and a second compartment, the first compartment containing a first component, the second compartment containing a second component, the components dimensioned to engage a spray gun, and
a mixing straw fluidly engaged to the first and second compartments, the mixing straw configured to receive and when the assembly is engaged with the spray gun and the spray gun is energized, combine the first and second components to form an uncured sealant mix and emit the uncured sealant mix, under pressure, from a tip of the mixing straw at a removed end thereof capable of curing to form a visibly clear, cured in place, sealant coat on an aircraft workpiece, the clear sealant coat being one of a polyurea, polyurethane or polyurea/polyurethane hybrid coat;
wherein the cured sealant coat is resistant to a phosphate ester based hydraulic fluid, and also resistant to Jet A fuel; the resistance to the phosphate ester based hydraulic fluid demonstrated by a weight change of 1.66% or less (24-hour spray) and the resistance to the Jet A fuel demonstrated by a weight change of 0.07% or less (24-hour spray).
2. The assembly of claim 1 , wherein the sealant coat cures to at least 85% of final hardness in 24 hours or less at 77° and 50% relative humidity.
3. The assembly of claim 1 , wherein the sealant coat has a hardness of between 20 and 80 Shore “A”.
4. The assembly of claim 1 , wherein the cured sealant coat is removable.
5. The assembly of claim 1 wherein the cured sealant coat has a tensile strength of greater than 100 psi.
6. The assembly of claim 1 wherein the cured sealant coat has an elasticity of at least 130%.
7. The assembly of claim 1 wherein the cured sealant coat is between 3 and 60 mil thick.
8. The assembly of claim 1 wherein the cured sealant coat undergoes a tint change during curing.
9. The assembly of claim 1 wherein the cured sealant coat is 3 to 60 mil thick and removable.
10. The assembly of claim 1 wherein the cured sealant coat is 3 to 60 mil thick and has an elasticity of at least 130%.
11. The assembly of claim 1 wherein the cured sealant coat is 3 to 60 mil thick and has a tensile strength of greater than 100 psi.
12. The assembly of claim 1 wherein the sealant coat cures to at least 85% of final hardness in 24 hours or less at 77° and 50% relative humidity and the cured sealant coat is between 3 and 60 mil thick.
13. The assembly of claim 1 wherein the sealant coat cures to at least 85% of final hardness in 24 hours or less at 77° and 50% relative humidity and the sealant coat has a hardness of between 20 and 80 Shore “A”.
14. The assembly of claim 1 wherein the sealant coat cures to at least 85% of final hardness in 24 hours or less at 77° and 50% relative humidity, the sealant coat has a hardness of between 20 and 80 Shore “A” and the cured sealant coat is between 3 and 60 mil thick.
15. The assembly of claim 1 wherein the cured sealant coat passes salt fog test (ASTM B117).
16. The assembly of claim 1 wherein the cured sealant coat is flame retardant (12 second vertical burn).
17. The assembly of claim 1 wherein the sealant coat is free of VOCs (Volatile Organic Compounds).
18. The assembly of claim 1 wherein the sealant coat has a peel strength of greater than 4 piw.
19. The assembly of claim 1 wherein the sealant is visually clear when coated to ¼″ thickness.
20. The assembly of claim 1 wherein the viscosity of the sealant mix, prior to gelling, is between about 700 and 1200 cps.