Increased resonant frequency alkali-doped Y-phase hexagonal ferrites
Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material, such as Y-phase hexagonal ferrite material, and methods of manufacturing. In some embodiments, sodium or potassium can be added into the crystal structure of the hexagonal ferrite material in order to achieve improved resonant frequencies in the range of 500 MHz to 1 GHz useful for radiofrequency applications.
1. A method for increasing the resonant frequency of a hexagonal ferrite material, the method comprising:
providing a Y phase hexagonal ferrite material including Sr, Co, Fe, and O, and having a strontium site and a crystal structure of an intergrowth between a magnetoplumbite and a spinel crystal structure;
doping the Y phase hexagonal ferrite material with sodium, potassium, or other univalent alkali metal on the strontium site; and
doping the Y phase hexagonal ferrite material with scandium or indium for charge compensating with the sodium, potassium, or other univalent alkali metal to form a doped Y phase hexagonal ferrite material.
2. The method of claim 1 , wherein aluminum is added into the crystal structure of the Y phase hexagonal ferrite material to replace the Fe.
3. The method of claim 2 , wherein the doped Y phase hexagonal ferrite material has a composition Sr 2 Co 2 Fe 12-y Al y O 22 or Sr 2-x (K,Na) x Co 2-x M x Fe 12-y Al y O 22 , with x being 0<x<2, y being 0<y<12 and M being the scandium or the indium.
4. The method of claim 3 , wherein the doped Y phase hexagonal ferrite material has the composition Sr 1.7 Na 0.3 Co 1.7 Sc 0.3 Fe 11.5 Al 0.5 O 22 or Sr 1.6 Na 0.4 Co 1.6 Sc 0.4 Fe 11.5 Al 0.5 O 22 .
5. The method of claim 1 , wherein the indium or the scandium are located on a cobalt site of the Y phase hexagonal ferrite material.
6. The method of claim 1 , further including incorporating silica into the Y phase hexagonal ferrite material.
7. The method of claim 1 , further including adding silicon into the crystal structure of the Y phase hexagonal ferrite material.
8. The method of claim 1 , further including adding manganese into the crystal structure of the Y phase hexagonal ferrite material.
9. The method of claim 8 , wherein the doped Y phase hexagonal ferrite material has a composition Sr 2 Co 2 Fe 12-y Mn y O 22 , Sr 2-x K x Co 2-x M x Fe 12-y Mn y O 22 or Sr 2-x K x Co 2-x M x Fe 12-y-z Mn y Al z O 22 with x being 0<x<2, y being 0<y<12, z being 0<z<12, (y+z) being 0<(y+z)<12, and M being the scandium or the indium.
10. The method of claim 1 , wherein the doped Y phase hexagonal ferrite material has a loss factor of less than about 6 at a frequency of 1 GHz.
11. The method of claim 1 , wherein sodium is doped into the Y phase hexagonal ferrite material.
12. The method of claim 1 , wherein potassium is doped into the Y phase hexagonal ferrite material.
13. The method of claim 1 , wherein the doped Y phase hexagonal ferrite material has a composition Sr 2-x K x Co 2-x M x Fe 12 O 22 or Sr 2-x Na x Co 2-x M x Fe 12 O 22 , with x being 0<x<2, and M being the scandium or the indium.
14. A doped ceramic material comprising:
a Y phase hexagonal ferrite material including Sr, Co, Fe, and O, and having a strontium site and a crystal structure of an intergrowth between a magnetoplumbite and a spinel crystal structure, the Y phase hexagonal ferrite material being doped with sodium, potassium, or other univalent alkali metal on the strontium site, and the Y phase hexagonal ferrite material being doped with scandium or indium for charge compensating with the sodium, potassium, or other univalent alkali metal to form a doped Y phase hexagonal ferrite material.
15. A radiofrequency device including a ceramic component, the radiofrequency device comprising:
a Y phase hexagonal ferrite material including Sr, Co, Fe, and O, and having a strontium site and a crystal structure of an intergrowth between a magnetoplumbite and a spinel crystal structure, the Y phase hexagonal ferrite material being doped with sodium, potassium, or other univalent alkali metal on the strontium site, and the Y phase hexagonal ferrite material being doped with scandium or indium for charge compensating with the sodium, potassium, or other univalent alkali metal to form a doped Y phase hexagonal ferrite material.
16. The radiofrequency device of claim 15 , wherein the ceramic radiofrequency device is an antenna.
17. The method of claim 3 , wherein x is 0<x≤1.5.
18. The method of claim 9 , wherein x is 0<x≤1.5.
19. The method of claim 13 , wherein x is 0<x≤1.5.