Ultra-high strength steel with excellent toughness
An ultra-high strength, high toughness alloy steel comprising, by weight, 0.24% to 0.32% carbon, 1.0% manganese or less, 0.45% silicon or less, 1.60% to 1.85% chromium, 2.5% to 3.1% nickel, 0.40% to 0.65% molybdenum, and 0.025% to 0.05% vanadium, the balance being iron and unavoidable impurities; or 0.23% to 0.28% carbon, 1.0% manganese or less, 0.45% silicon or less, 2.05% to 2.4% chromium, 0.35% or less nickel, 0.85% to 1.15% molybdenum, and 0.03% or less vanadium, the balance being iron and unavoidable impurities; or 0.27% to 0.32% carbon, 1.0% manganese or less, 0.45% silicon or less, 0.7% to 1.0% chromium, 0.7% to 1.0% nickel, 0.7% to 1.0% molybdenum, 0.05% or less vanadium, and 0.05% or less niobium, the balance being iron and unavoidable impurities.
1. An alloy steel consisting of, by weight:
0.24% to 0.32% carbon;
1.0% manganese or less;
0.45% silicon or less;
1.60% to 1.85% chromium;
2.5% to 3.1% nickel;
0.40% to 0.65% molybdenum;
0.025% to 0.05% vanadium; and
0.01% niobium or less,
the balance being iron and unavoidable impurities,
wherein the room temperature, longitudinal Charpy impact energy toughness is 35 ft.-lbs. or more.
2. The alloy steel of claim 1 , wherein the ultimate tensile strength is 200 KSI or more, the 0.2% offset yield strength is 170 KSI or more, and the hardness on the Rockwell C scale is 40 or more.
3. The alloy steel of claim 1 , wherein the −40° F., longitudinal Charpy impact energy toughness is 25 ft.-lbs. or more.
4. The alloy steel of claim 1 , wherein the elongation to failure is 12% or more and the reduction of area at failure is 35% or more.
5. The alloy steel of claim 1 , wherein the smooth sample rotating bending fatigue strength is 85 KSI or more.
6. The alloy steel of claim 1 , wherein the microstructure of the alloy steel comprises at least 90% martensite.
7. The alloy steel of claim 1 , wherein the unavoidable impurities include, in weight %, 0.035% or less aluminum, 0.012% or less nitrogen, 0.25% or less copper, 0.025% or less sulfur, 0.002% or less Ca, 0.0015% or less oxygen, 0.012% or less phosphorus, 0.012% or less tin, 0.012% or less arsenic and 0.012% or less antimony.
8. An alloy steel consisting of, by weight:
0.23% to 0.28% carbon;
1.0% manganese or less;
0.45% silicon or less;
2.05% to 2.4% chromium;
0.35% or less nickel;
0.85% to 1.15% molybdenum;
0.03% or less vanadium; and
0.01% niobium or less,
the balance being iron and unavoidable impurities.
9. The alloy steel of claim 8 , wherein the ultimate tensile strength is 220 KSI or more, the 0.2% offset yield strength is 175 KSI or more, the hardness on the Rockwell C scale is 42 or more.
10. The alloy steel of claim 8 , wherein the room temperature, longitudinal Charpy impact energy toughness is 35 ft.-lbs. or more and the −49° F., longitudinal Charpy impact energy toughness is 35 ft.-lbs. or more.
11. The alloy steel of claim 8 , wherein the elongation to failure is 13% or more and the reduction of area at failure is 40% or more.
12. The alloy steel of claim 8 , wherein the U-notched rotating bending fatigue strength when K t =1.5 is 90 KSI or more.
13. The alloy steel of claim 8 , wherein the microstructure of the alloy steel comprises at least 90% martensite.
14. The alloy steel of claim 8 , wherein the unavoidable impurities include, in weight percent, 0.035% or less aluminum, 0.012% or less nitrogen, 0.25% or less copper, 0.025% or less sulfur, 0.002% or less Ca, 0.0015% or less oxygen, 0.012% or less phosphorus, 0.012% or less tin, 0.012% or less arsenic and 0.012% or less antimony.
15. An alloy steel consisting of, by weight:
0.27% to 0.32% carbon;
1.0% manganese or less;
0.45% silicon or less;
0.7% to 1.0% chromium;
0.7% to 1.0% nickel;
0.7% to 1.0% molybdenum;
0.05% or less vanadium; and
0.05% or less niobium,
the balance being iron and unavoidable impurities,
wherein the room temperature, longitudinal Charpy impact energy toughness is 30 ft.-lbs. or more.
16. The alloy steel of claim 15 , wherein the ultimate tensile strength is 235 KSI or more, the 0.2% offset yield strength is 195 KSI or more, and the hardness on the Rockwell C scale is 42 or more.
17. The alloy steel of claim 15 , wherein the −40° F., longitudinal Charpy impact energy toughness is 25 ft.-lbs. or more.
18. The alloy steel of claim 15 , wherein the elongation to failure is 12% or more and the reduction of area at failure is 40% or more.
19. The alloy steel of claim 15 , wherein the smooth sample rotating bending fatigue strength is 80 KSI or more.
20. The alloy steel of claim 15 , wherein the microstructure of the alloy steel comprises at least 90% martensite.
21. The alloy steel of claim 15 , wherein the unavoidable impurities include, in weight %, 0.035% or less aluminum, 0.012% or less nitrogen, 0.25% or less copper, 0.025% or less sulfur, 0.002% or less Ca, 0.0015% or less oxygen, 0.012% or less phosphorus, 0.012% or less tin, 0.012% or less arsenic and 0.012% or less antimony.