View Patent ↗A primary object of this invention is to provide a continuous casting method by which a slab of excellent internal quality can be obtained even if the casting speed is changed. In this invention, upon continuous casting with two pairs of the reduction rolls arranged along a casting direction and support rolls arranged between the reduction rolls, when a casting speed is reduced compared to a state where combination of reduction with reduction rolls at a first stage on an unsolidified portion of the slab and reduction with reduction rolls at a second stage on a solidified portion thereof is employed, the combination is switched to combination of reduction with the reduction rolls at the first stage on a portion of the slab at an end of solidification and the reduction with the reduction rolls at the second stage on the solidified portion thereof.
1. A method for continuous-casting a slab while reduction is carried out on the slab using a continuous casting machine with two stages of reduction rolls, each of the two stages consisting of a pair of the reduction rolls, and being arranged along a casting direction, a diameter of each of the reduction rolls being 1.2 to 2.0 times as much as thickness of the slab just before reduction with corresponding reduction rolls, the continuous casting machine including the reduction rolls and support rolls, the support rolls being arranged between said two stages of the reduction rolls, the method comprising;
increasing a casting speed compared to a state where the slab is cast at a constant speed under combination of reduction with reduction rolls at a first stage on a portion of the slab at an end of solidification, a solid-phase ratio of the portion at a center of the slab in a thickness direction being no less than 0.8 and less than 1.0, and reduction with reduction rolls at a second stage on a solidified portion of the slab, a solid-phase ratio of the solidified portion at the center of the slab in the thickness direction being 1.0, the reduction rolls at the second stage being arranged more downstream than the reduction rolls of the first stage in the casting direction, and
switching the combination to a combination of reduction with the reduction rolls at the first stage on an unsolidified portion of the slab, a solid-phase ratio of the unsolidified portion at the center of the slab in the thickness direction being less than 0.8, with an adjusted reduction amount of the reduction rolls at the first stage, and the reduction with the reduction rolls at the second stage on the solidified portion of the slab, the solid-phase ratio of the solidified portion at the center of the slab in the thickness direction being 1.0, accompanying movement of a place of the slab where the solidification is ended downstream in the casting direction due to the increase of the casting speed.