Supports for sintering additively manufactured parts
According to one aspect, embodiments herein provide a method comprising forming a shrinking platform of model material above a build plate, the model material including sinterable metal particles and a first binder, forming a support structure of the model material extending up from the shrinking platform, forming a first portion of the part from successive layers of the model material above the support structure, forming a release layer intervening between a surface of the part and an opposing surface of the support structure or between a surface of the shrinking platform and an opposing surface of the build plate, the release layer including a dispersed ceramic powder and a second binder, and supporting the part, the release layer, and the support structure upon the shrinking platform to form a platform-integrating part assembly, the support structure being configured to prevent the first portion from distorting from gravitational force during sintering.
1. A method of reducing distortion in an additively manufactured part, comprising:
forming a sintering tray of a first composite material above a build plate, the first composite material including a metal particulate filler in a first debindable matrix;
forming sintering supports of the first composite material extending up from the sintering tray, wherein the sintering supports are configured to support the part during a sintering process to prevent it from being distorted due to gravitational force;
forming the part through depositing successive layers of the first composite material above the sintering tray;
forming a separation layer of a second composite material, wherein the second composite material includes a ceramic particulate filler in a second debindable matrix, and wherein the separation layer is configured to intervene between a surface of the part and an opposing surface of the sintering supports, between a bottom surface of the part and a top surface of the sintering tray, or between a bottom surface of the sintering tray and a top surface of the build plate;
forming from the sintering tray, the sintering supports, the separation layer, and the part, a portable assembly;
debinding the portable assembly during a debinding process; and
heating, during the sintering process, the portable assembly to a temperature sufficient to simultaneously:
sinter and densify the sintering tray, the sintering supports, and the part together at a uniform rate; and
powderize the separation layer to leave loose ceramic particulate between opposing surfaces.
2. The method according to claim 1 , wherein forming the separation layer comprises forming the separation layer intervening between a non-horizontal surface of the part and the opposing surface of the sintering supports, the non-horizontal surface of the part including at least one of a vertical surface, a curved surface, and a surface angled with respect to a horizontal plane.
3. The method according to claim 1 , further comprising:
debinding the first debindable matrix and the second debindable matrix within the portable assembly simultaneously and in a same chamber.
4. The method according to claim 1 , further comprising:
separating the surface of the part and the opposing surface of the sintering supports with the loose ceramic particulate and allowing the part to be readily removed from the sintering supports after the sintering process.
5. The method according to claim 1 , wherein forming the sintering tray further comprises:
forming the sintering tray to form a foundation for the sintering supports and the part; and
forming the sintering tray to hold the part and the sintering supports in relative position during the sintering process to prevent movement of the sintering supports against the part.
6. The method according to claim 1 , further comprising:
interconnecting the first composite material of the sintering tray to the first composite material of the sintering supports to permit mass diffusion between metal particles found in the sintering tray and adjacent metal particles found in the sintering supports, to unitarily densify the sintering tray and the sintering supports.
7. A method of reducing distortion in an additively manufactured part, comprising:
forming a sintering tray of a composite material above a build plate, the composite material including a metal particulate filler in a first debindable matrix;
forming sintering supports of the composite material extending up from the sintering tray;
forming the part through depositing successive layers of the composite material above the sintering tray;
forming a separation layer intervening between a bottom surface of the sintering tray and a top surface of the build plate;
forming from the sintering tray, the sintering supports, the separation layer, and the part, a portable assembly, wherein the portable assembly is configured to be debound and sintered as a whole, and the sintering supports are configured to prevent the part from distorting during a sintering process due to gravitational force; and
allowing, via the separation layer, the sintering tray to slide on the build plate as the sintering tray shrinks during the sintering process to reduce distortion to the part.
8. The method according to claim 7 , wherein forming the sintering tray further comprises:
forming the sintering tray to form a foundation for the sintering supports and the part; and
forming the sintering tray to hold the part and the sintering supports in relative position during the sintering process to prevent movement of the sintering supports against the part.
9. The method according to claim 7 , further comprising:
interconnecting the first composite material of the sintering tray to the first composite material of the sintering supports to permit mass diffusion between metal particles found in the sintering tray and adjacent metal particles found in the sintering supports, to unitarily densify the sintering tray and the sintering supports.
10. The method according to claim 7 , wherein forming the separation layer includes forming the separation layer with a separation material that includes a ceramic particulate filler in a second debindable matrix.
11. The method according to claim 10 , wherein allowing the sintering tray to slide during the sintering process includes powderizing the separation layer during the sintering process to leave loose ceramic particulate between the bottom surface of the sintering tray and the top surface of the build plate.
12. The method according to claim 10 , further comprising:
debinding the first debindable matrix and the second debindable matrix within the portable assembly simultaneously and in a same chamber.
13. The method according to claim 10 , further comprising:
forming a second separation layer of the separation material configured to intervene between a surface of the part and an opposing surface of the sintering supports or between a bottom surface of the part and a top surface of the sintering tray; and
powderizing the second separation layer during the sintering process to leave loose ceramic particulate.
14. The method according to claim 13 , further comprising:
separating the surface of the part and the opposing surface of the sintering supports with the loose ceramic particulate and allowing the part to be readily removed from the sintering supports after the sintering process.
15. A method of reducing distortion in an additively manufactured part, comprising:
forming a sintering tray of a composite material above a build plate, wherein the composite material includes a metal particulate filler in a first debindable matrix, and wherein the sintering tray is formed to be laterally larger than the part;
forming sintering supports of the composite material extending up from the sintering tray;
forming the part through depositing successive layers of the composite material above the sintering tray;
forming the sintering tray, the sintering supports, and the part to substantially align a centroid of the combined sintering tray and sintering supports with a centroid of the part;
forming a separation layer intervening between a surface of the part and an opposing surface of the sintering supports, between a bottom surface of the part and a top surface of the sintering tray, or between a bottom surface of the sintering tray and a top surface of the build plate; and
forming from the sintering tray, the sintering supports, the separation layer, and the part a portable assembly, wherein the portable assembly is configured to be debound and sintered as a whole, and the sintering supports are configured to prevent the part from distorting during a sintering process due to gravitational force.
16. The method according to claim 15 , wherein forming the-sintering tray further comprises:
forming the sintering tray to form a foundation for the sintering supports and the part; and
forming the sintering tray to hold the part and the sintering supports in relative position during the sintering process to prevent movement of the sintering supports against the part.
17. The method according to claim 15 , wherein forming the separation layer comprises forming the separation layer intervening between a non-horizontal surface of the part and the surface of the sintering supports, the non-horizontal surface of the part including at least one of a vertical surface, a curved surface, and a surface angled with respect to a horizontal plane.
18. The method according to claim 15 , wherein forming the separation layer includes forming the separation layer with a separation material that includes a ceramic particulate filler in a second debindable matrix.
19. The method according to claim 18 , further comprising:
debinding the first debindable matrix and the second debindable matrix within the portable assembly simultaneously and in a same chamber; and
heating, during the sintering process, the platform assembly to a temperature sufficient to simultaneously sinter and densify the sintering tray, the sintering supports, and the part together at a uniform rate, and to powderize the separation layer to leave a loose ceramic particulate between the opposing surfaces.
20. The method according to claim 19 , further comprising:
separating the surface of the part and the opposing surface of the sintering supports with the loose ceramic particulate and allowing the part to be readily removed from the sintering supports after the sintering process.