Quantum dot film
A quantum dot film includes a plurality of sealed microcells. The microcells may be formed within a layer of polymeric material and sealed with a sealing material. Also, the microcells may contain a dispersion of a solvent and a plurality of quantum dots. A method of making a quantum dot film includes providing a layer of polymeric material having a plurality of open microcells, filling the plurality of open microcells with a dispersion of a solvent and plurality of quantum dots, and sealing the microcells.
1. A quantum dot film comprising a plurality of sealed microcells, the microcells being formed within a layer of polymeric material and sealed with a sealing material, and the microcells containing a dispersion comprising a solvent and a plurality of quantum dots,
wherein the sealing material is selected from the group consisting of monofunctional acrylates; monofunctional methacrylates; multifunctional acrylates; multifunctional methacrylates; polyvinyl alcohol; polyacrylic acid; gelatin; polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol, and derivatives thereof; poly(vinylpyrolidone) and copolymers thereof; polysaccharides and derivatives thereof; melamine-formaldehyde; poly(acrylic acid) and salt forms and copolymers thereof; poly(methacrylic acid) and salt forms and copolymers thereof; poly(maleic acid) and salt forms and copolymers thereof; poly(2-dimethylaminoethyl methacrylate); poly(2-ethyl-2-oxazoline); poly(2-vinylpyridine); poly(allylamine); polyacrylamide; polyethylenimine; polymethacrylamide; poly(sodium styrene sulfonate); cationic polymers functionalized with quaternary ammonium groups; polyurethane water dispersions; and latex water dispersions.
2. The quantum dot film of claim 1 , wherein the polymeric material is selected from the group consisting of a thermoplastic and a thermoset.
3. The quantum dot film of claim 1 , wherein the sealing material is light transmissive.
4. The quantum dot film of claim 1 , wherein the solvent comprises a liquid.
5. The quantum dot film of claim 1 , wherein the dispersion comprises 0.01 to 10% wt. quantum dots.
6. The quantum dot film of claim 1 , wherein the quantum dots comprise nanocrystals selected from the group consisting of CdSe/ZnS, InP/ZnS, PbSe/PbS, CdSe/CdS, CdTe/CdS and CdTe/ZnS.
7. An electro-optic display comprising a quantum dot film according to claim 1 .
8. The electro-optic display of claim 7 further comprising a light-emitting layer and a color filter layer, wherein the quantum dot film is disposed between the light-emitting layer and the color filter layer.
9. The electro-optic display of claim 8 , further comprising a layer of shuttering media selected from the group consisting of liquid crystal, a di-electrophoretic dispersion, and electrochromic material.
10. A method of making a quantum dot film comprising:
providing a layer of polymeric material having a plurality of open microcells;
filling the plurality of open microcells with a dispersion comprising a solvent and plurality of quantum dots; and
sealing the microcells,
wherein the sealing material is selected from the group consisting of monofunctional acrylates; monofunctional methacrylates; multifunctional acrylates; multifunctional methacrylates; polyvinyl alcohol; polyacrylic acid; gelatin; polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol, and derivatives thereof; poly(vinylpyrolidone) and copolymers thereof; polysaccharides and derivatives thereof; melamine-formaldehyde; poly(acrylic acid) and salt forms and copolymers thereof; poly(methacrylic acid) and salt forms and copolymers thereof; poly(maleic acid) and salt forms and copolymers thereof; poly(2-dimethylaminoethyl methacrylate); poly(2-ethyl-2-oxazoline); poly(2-vinylpyridine); poly(allylamine); polyacrylamide; polyethylenimine; polymethacrylamide; poly(sodium styrene sulfonate); cationic polymers functionalized with quaternary ammonium groups; polyurethane water dispersions; and latex water dispersions.
11. The method of claim 10 , wherein the providing step comprises embossing the plurality of open microcells into the layer of polymeric material.
12. The method of claim 10 , wherein the dispersion further comprises a curable compound and the sealing step comprises curing the curable compound to form a sealing layer and contain the solvent and plurality of quantum dots within the sealed microcells.
13. A quantum dot film comprising a plurality of sealed microcells, the microcells being formed within a layer of polymeric material and sealed with a sealing material, and the microcells containing a dispersion comprising a solvent and a plurality of quantum dots,
wherein the quantum dots comprise nanocrystals selected from the group consisting of CdSe/ZnS, InP/ZnS, PbSe/PbS, CdSe/CdS, CdTe/CdS and CdTe/ZnS.
14. The quantum dot film of claim 13 , wherein the polymeric material is selected from the group consisting of a thermoplastic and a thermoset.
15. The quantum dot film of claim 13 , wherein the sealing material is selected from the group consisting of monofunctional acrylates; monofunctional methacrylates; multifunctional acrylates; multifunctional methacrylates; polyvinyl alcohol; polyacrylic acid; gelatin; polyethylene glycol, copolymers of polyethylene glycol and polypropylene glycol, and derivatives thereof; poly(vinylpyrolidone) and copolymers thereof; polysaccharides and derivatives thereof; melamine-formaldehyde; poly(acrylic acid) and salt forms and copolymers thereof; poly(methacrylic acid) and salt forms and copolymers thereof; poly(maleic acid) and salt forms and copolymers thereof; poly(2-dimethylaminoethyl methacrylate); poly(2-ethyl-2-oxazoline); poly(2-vinylpyridine); poly(allylamine); polyacrylamide; polyethylenimine; polymethacrylamide; poly(sodium styrene sulfonate); cationic polymers functionalized with quaternary ammonium groups; polyurethane water dispersions; and latex water dispersions.
16. The quantum dot film of claim 15 , wherein the sealing material is light transmissive.
17. The quantum dot film of claim 13 , wherein the solvent comprises a liquid.
18. The quantum dot film of claim 13 , wherein the dispersion comprises 0.01 to 10% wt. quantum dots.
19. An electro-optic display comprising a quantum dot film according to claim 13 .
20. The electro-optic display of claim 19 further comprising a light-emitting layer and a color filter layer, wherein the quantum dot film is disposed between the light-emitting layer and the color filter layer.
21. The electro-optic display of claim 20 , further comprising a layer of shuttering media selected from the group consisting of liquid crystal, a di-electrophoretic dispersion, and electrochromic material.
22. A method of making a quantum dot film comprising:
providing a layer of polymeric material having a plurality of open microcells;
filling the plurality of open microcells with a dispersion comprising a solvent and plurality of quantum dots; and
sealing the microcells,
wherein the quantum dots comprise nanocrystals selected from the group consisting of CdSe/ZnS, InP/ZnS, PbSe/PbS, CdSe/CdS, CdTe/CdS and CdTe/ZnS.
23. The method of claim 22 , wherein the providing step comprises embossing the plurality of open microcells into the layer of polymeric material.
24. The method of claim 22 , wherein the dispersion further comprises a curable compound and the sealing step comprises curing the curable compound to form a sealing layer and contain the solvent and plurality of quantum dots within the sealed microcells.